The effect of iron and yttrium additions on glass forming ability and corrosion resistance of Al₈₈Y_8-xFe_4+x (x = 0, 1, 2 at.%) alloys in the form of ingots and melt-spun ribbons was investigated. The crystalline multiphase structure of ingots and amorphous-crystalline structure of ribbons were examined by a number of analytical techniques including X-ray diffraction, Mössbauer spectroscopy, and transmission electron microscopy. It was confirmed that the higher Fe additions contributed to formation of amorphous structures. The impact of chemical composition and structure of alloys on their corrosion resistance was characterized by electrochemical tests in 3.5% NaCl solution at 25 °C. The identification of the mechanism of chemical reactions taking place during polarization test along with the morphology and internal structure of the surface oxide films generated was performed. It was revealed that the best corrosion resistance was achieved for the Al₈₈Y₇Fe₅ alloy in the form of ribbon, which exhibited the lowest corrosion current density (j_corr = 0.09 μA/cm²) and the highest polarization resistance (R_p = 96.7 kΩ∙cm²).

Medium-entropy alloys (MEAs) exhibit properties comparable or even superior to high-entropy alloys (HEAs). Due to their very good resistance in thermomechanical conditions and corrosive environments and unique electrical and magnetic properties, medium-entropy alloys are good candidates for coating applications. One of the most economically effective methods of producing metallic coatings is electrodeposition. In this work, the structure of an electrodeposited CoFeNi medium-entropy alloy coating on a copper substrate from a metal chlorides solution (FeCl₂ ∙ 4H₂O + CoCl₂ ∙ 6H₂O + NiCl₂ ∙ 6H₂O) with the addition of boric acid (H₃BO₃) was investigated. The coating was characterized by a nanocrystalline structure identified by transmission electron microscopy examination and X-ray diffraction methods. Based on XRD and TEM, the face-centered cubic (FCC) phase of the CoFeNi MEA coating was identified. The high corrosion resistance of the MEA coating in a 3.5% NaCl environment at 25 °C was confirmed by electrochemical tests.

Al-Y-Fe amorphous and nanocrystalline alloys are characterized by a unique collection of diverse properties that are influenced by various factors, including heat treatment. In this paper, the effect of heat treatment on the structural changes and selected properties of Al-Y-Fe metallic glasses in the as-spun state is investigated. The structure of the Al88Y7Fe5 and Al88Y6Fe6 alloys was examined by X-ray diffraction (XRD) and Mössbauer spectroscopy (MS). The corrosion resistance of the samples was characterized using polarization tests in a 3.5% NaCl solution at 25 °C. The effect of sodium chloride on the surface was studied with scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). The magnetic properties of Al-based alloys were explored using a vibrating sample magnetometer (VSM). It was revealed that the tested alloys show better properties after annealing than in the as-spun state. The annealing of the Al88Y7Fe5 and Al88Y6Fe6 alloys in the temperature range of 200 to 300 °C improved the magnetic properties and corrosion resistance of these materials. After 3,600 s, the better EOCP values were recorded for the Al88Y6Fe6 and Al88Y7Fe5 alloys after annealing at 300 °C and 200 °C, adequately. On the basis of the polarization tests, it was concluded that the electrochemical properties are better for Al88Y6Fe6 alloys after annealing at 300 °C.