Direct hydrogenation of CO₂ to methanol is an interesting method to recycle CO₂ emitted e.g., during combustion of fossil fuels. However, it is a challenging process because both the selectivity to methanol and its production are low. The metal-organic frameworks are relatively new class of materials with a potential to be used as catalysts or catalysts supports, also in the reaction of MeOH production. Among many interesting structures, the UiO-66 draws significant attention owing to its chemical and thermal stability, developed surface area, and the possibility of tuning its properties e.g., by exchanging the zirconium in the nodes to other metal cations. In this work we discuss—for the first time—the performance of Cu supported on UiO-66(Ce/Zr) in CO₂ hydrogenation to MeOH. We show the impact of the composition of UiO-66-based catalysts, and the character of Cu-Zr and Cu-Ce interactions on MeOH production and MeOH selectivity during test carried out for 25 h at T = 200 °C and p = 1.8 MPa. Significant increase of selectivity to MeOH was noticed after exchanging half of Zr⁴⁺ cations with Ce⁴⁺; however, no change in MeOH production occurred. It was found that the Cu-Ce coexistence in the UiO-66-based catalytic system reduced the selectivity to MeOH when compared to Cu/UiO-66(Zr), which was ascribed to lower concentration of Cu⁰ active sites in Cu/UiO-66(Ce/Zr), and this was caused by oxygen spill-over between Cu⁰ and Ce⁴⁺, and thus, the oxidation of the former. The impact of reaction conditions on the structure stability of tested catalyst was also determined.

The chemical stability and adsorptive/catalytic properties of the most widely studied metal–organic framework (MOF), which is HKUST-1, can be improved by its combination with graphene oxide (GO) or reduced graphene oxide (rGO). The chemistry of GO or rGO surfaces has a significant impact on their interaction with MOFs. In this work, we demonstrate that GO and rGO interaction with HKUST-1 influences the morphology and textural properties but has no impact on the thermal stability of the final composites. We also show that synthesis environment, e.g., stirring, to some extent influences the formation of HKUST-1/GO and HKUST-1/rGO composites. Homogeneous samples of the sandwich-type composite can be obtained when using reduced graphene oxide decorated with copper (Cu/rGO), which, owing to the presence of Cu sites, allows the direct crystallisation of HKUST-1 and its further growth on the graphene surface. This work is the first part of our research on HKUST-1/GO and HKUST-1/rGO and deals with the influence of the type of graphene material and synthesis parameters on the composites’ physicochemical properties that were determined by using X-ray diffraction, scanning and transmission electron microscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and thermogravimetric analysis.

The synthesis method of metal–organic frameworks (MOFs) has an important impact on their properties, including their performance in catalytic reactions. In this work we report on how the performance of [Cu₃(TMA)₂(H₂O)₃]_n (HKUST-1) and Ce@HKUST-1 in the reaction of CO oxidation depends on the synthesis method of HKUST-1 and the way the cerium active phase is introduced to it. The HKUST-1 is synthesised in two ways: via the conventional solvothermal method and in the presence of a cationic surfactant (hexadecyltrimethylammonium bromide (CTAB)). Obtained MOFs are used as supports for cerium oxide, which is deposited on their surfaces by applying wet and incipient wetness impregnation methods. To determine textural properties, structure, morphology, and thermal stability, the HKUST-1 supports and Ce@HKUST-1 catalysts are characterised using X-ray diffraction (XRD), N₂ sorption, scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), and thermogravimetric analysis (TGA). It is proven that the synthesis method of HKUST-1 has a significant impact on its morphology, surface area, and thermal stability. The synthesis method also influences the dispersion and the morphology of the deposited cerium oxide. Last but not least, the synthesis method affects the catalytic activity of the obtained material.

This paper describes the effect of calcination temperature on the phase composition, chemical composition, and morphology of ZrO₂ and Al₂O₃ powders modified with 3-aminopropyltriethoxysilane (APTES). Both ceramic powders were modified by etching in piranha solution, neutralization in ammonia water, reaction with APTES, ultrasonication, and finally calcination at 250, 350, or 450 °C. The obtained modified powders were characterized using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, particle size distribution (PSD), scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM/EDS), and thermogravimetric analysis (TGA).

This work aimed to prepare a composite with a polyamide (PA) matrix and surface-modified ZrO₂ or Al₂O₃ to be used as ceramic fillers (CFs). Those composites contained 30 wt.% ceramic powder to 70 wt.% polymer. Possible applications for this type of composite include bioengineering applications especially in the fields of dental prosthetics and orthopaedics. The ceramic fillers were subjected to chemical surface modification with Piranha Solution and suspension in 10 M sodium hydroxide and Si₃N₄ to achieve the highest possible surface development and to introduce additional functional groups. This was to improve the bonding between the CFs and the polymer matrix. Both CFs were examined for particle size distribution (PSD), functional groups (FTIR), chemical composition (XPS), phase composition (XRD), and morphology and chemical composition (SEM/EDS). Filaments were created from the powders prepared in this way and were then used for 3D FDM printing. Samples were subjected to mechanical tests (tensility, hardness) and soaking tests in a high-pressure autoclave in artificial saliva for 14, 21, and 29 days.