The aim of this paper is to evaluate the feasibility of obtaining alumina from boehmite using a free, clean, and unlimited power source as the solar energy. Boehmite was obtained by hydrothermal treatment of a hazardous waste coming from aluminum slag milling. The waste is considered as a hazardous substance because of it releasing toxic gases (hydrogen, ammonia, methane, and hydrogen sulfide) in the presence of water. The as-obtained boehmite was transformed into alumina, in air atmosphere, using a solar energy concentrator (Fresnel lens). The solar installation provides a power density of 260 W·cm⁻²which allows reaching temperatures upper than 1000°C at few minutes of exposure. Tests were performed at different periods of time that ranged between 5 and 90 min. The percentage of transformation of boehmite into alumina was followed by the water content of samples after solar radiation exposure. Samples were characterized by X-ray diffraction, infrared spectroscopy, and thermogravimetry. Metastable aluminas started to appear at 5 min and the crystalline and stable phase corundum at 10 min of solar radiation exposure.

Friction stir processing (FSP) was used on coarse-grained WE54 magnesium alloy plates of as-received material. These were subjected to FSP under two different cooling conditions, refrigerated and non-refrigerated, and different severe processing conditions characterized by low rotation rate and high traverse speed. After FSP, ultrafine equiaxed grains and refinement of the coarse precipitates were observed. The processed materials exhibited high resistance at room temperature and excellent superplasticity at the high strain rate of 10⁻² s⁻¹ and temperatures between 300 and 400 °C. Maximum tensile superplastic elongation of 726% was achieved at 400 °C. Beyond 400 °C, a noticeable loss of superplastic response occurred due to a loss of thermal stability of the grain size. Grain boundary sliding is the operative deformation mechanism that can explain the high-temperature flow behavior of the ultrafine grained FSP-WE54 alloy, showing increasing superplasticity with increasing processing severity.