Fiber-reinforced asphalt mixture has been widely used in pavement engineering to not only prevent asphalt binder leakage but also improve engineering properties of asphalt mixture. However, the research on three key parameters, namely fiber type, fiber length, and fiber content, which significantly affect the performance of fiber-reinforced asphalt mixture, have seldom been conducted systematically. To determine these three key parameters in the support of the application of fibers in mixture scientifically, three commonly used fibers were selected, basalt fiber, polyester fiber, and lignin fiber, and the testing on fibers, fiber-reinforced asphalt binders, and fiber-reinforced asphalt mixtures was conducted afterwards. The results showed: the favorable fiber type was basalt fiber; the favorable basalt fiber length was 6mm; the engineering properties including high temperature stability, low temperature crack resistance, and water susceptibility were clearly improved by the added basalt fiber, and the optimum basalt fiber content was 0.4 wt.%. The obtained results may be valuable from a practical point of view to engineers and practitioners.

In this project, the adhesion property and moisture effect between styrene–butadiene–styrene (SBS) modified asphalt binder and aggregate were studied to reveal their interface adhesion mechanism. The influence of SBS contents on adhesion property and moisture effect between binder and aggregate phases were investigated using molecular dynamics simulation. Moreover, the double-layer adhesion models of asphalt binder–aggregate and triple-layer debonding models of asphalt binder–water–aggregate were constructed and equilibrated, and the adhesion property and the moisture effect were evaluated numerically. The results indicate that the built SBS-modified asphalt binder models show favorable reliability in representing the real one. The variation in the work of adhesion for SBS modified asphalt binder–quartz is not remarkable with the SBS content when its content is relatively low. However, the work of adhesion decreased significantly when the content was higher than 6 wt.%, which is consistent with the experimental results. The adhesion between SBS-modified asphalt binder and quartz is derived from Van der Waals energy. The modified asphalt binder with a high SBS modifier content (8 wt.% and 10 wt.%) shows much better moisture resistance (nearly 30% improved) than the unmodified asphalt binder from the work of debonding results. According to the Energy Ratio (ER) values, asphalt binders with high SBS content (8 wt.% and 10 wt.%) present a good moisture resistance performance. Therefore, the SBS content should be seriously selected by considering the dry and wet conditions that are used to balance the adhesion property and debonding properties. The content of 4 wt.% may be the optimal content under the dry adhesion and moisture resistance.

High-modulus asphalt mixture (HMAM) is one of the most effective materials to enhance the rutting resistance of asphalt pavement and upgrade pavement sustainability. The objectives of this study are to investigate the modulus properties of different HMAMs and their correlation with the rutting resistance, to propose reasonable modulus evaluation indicators, and to analyze the rutting resistance mechanisms of different materials (hard asphalt, polyethylene, dissolved polyolefin). The effect of three HMAMs and two styrene-butadiene-styrene (SBS) modifiers on asphalt mixtures’ rutting resistance were evaluated by dynamic modulus test and wheel track test, and the results were simulated and further analyzed via ABAQUS. The results indicate that the dynamic modulus of the mixtures showed a gradual increase and decrease with the increase of loading frequency and testing temperature, respectively. The ratio of dynamic modulus in low frequency to that in high frequency correlates well with dynamic stability under high-temperature conditions, and the wider the frequency coverage, the higher the correlation between this ratio and dynamic stability. The rutting resistance of asphalt pavements can be improved by reducing the frequency sensitivity of HMAMs under high temperatures or by increasing the modulus’ absolute value of the pavement structural layer. Therefore, two indicators, the absolute value of the modulus and the ratio of 0.1 Hz dynamic modulus to 25 Hz dynamic modulus at 55 °C, are recommended for the evaluation of rutting resistance of HMAMs. Based on the evaluation indexes proposed in this paper, a comparative analysis of the rutting resistance mechanism of HMAMs prepared with different materials was carried out, and it was concluded that the mixture with high-modulus agents had the best rutting resistance, which is consistent with the test road observations, thus verifying the feasibility of the modulus evaluation indexes recommended in this paper for the evaluation of the rutting resistance of different types of HMAMs.

Cement-stabilized macadam (CEM-SM) base layers on highways are prone to early shrinkage cracking in extremely cold and arid regions, mainly caused by the large drying shrinkage of traditional cement-stabilized base materials. A multi-component solid waste cementitious material (SWCM) was designed based on the response surface method. The synergistic reaction mechanism of SWCM was analyzed using X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FT-IR) and thermogravimetric analysis (TG). A shrinkage testing system was developed to evaluate the anti-cracking characteristics of stable macadam using multiple solid waste cementitious materials (SWCM-SM), and the strength growth law and frost resistance were analyzed. The results show that the Box–Behnken response surface model was used to obtain the optimal parameter combination for SWCM, including 60% slag, 30% steel slag, and 10% desulfurization gypsum. The compressive strength and flexural strength of SWCM-SM were 24.1% and 26.7% higher than those of CEM-SM after curing 180 days. The frost resistance of SWCM-SM was basically equivalent to that of CEM-SM, and the dry shrinkage strain of SWCM-SM was reduced by 30.7% compared to CEM-SM. It can be concluded that steel slag and desulfurization gypsum stimulate the hydration reaction of slag, thereby improving the bonding strength. Compared to CEM-SM, SWCM-SM exhibits slower hydration reaction and longer hydration duration, exhibiting characteristics of low early strength and high later strength. The early microstrain of the semi-rigid base layer is mainly caused by the occurrence of early water loss shrinkage, and the water loss rate of SWCM-SM is lower than that of CEM-SM. This study concludes that SWCM has good early crack resistance performance for stabilized crushed stones.

The regeneration performance of an aged styrene–butadiene–styrene block copolymer (SBS) will be significantly influenced by different rejuvenators. The objective of this study was to comparatively investigate the regeneration effect of different SBS-modified asphalt regenerators on aged SBS-modified asphalt. Four types of different regenerant formulations were selected. The optimal rejuvenator content was determined firstly using conventional performance tests. The rheological properties of the aged SBS-modified asphalt binder were evaluated by multiple stress creep recovery (MSCR) experiments. Subsequently, the regeneration mechanism of the SBS-modified asphalt binder was investigated using thin-layer chromatography–flame ionization detection (TLC-FID) and Fourier transform infrared spectroscopy (FTIR). The results showed that the rejuvenator had a certain recovery effect on the penetration, softening point, and ductility of the SBS-modified asphalt binder after aging. The SBS-modified rejuvenating agent was the most favorable among the four types of rejuvenators, where a rejuvenator dosage of 12% showed the optimal rejuvenation effect. The addition of regenerators could appropriately improve the elastic deformation capacity of the aged asphalt binder. The epoxy soybean oil in the regenerant reacted with the aging SBS-modified asphalt binder, supplementing the lost oil in the aged SBS-modified asphalt binder, dispersing the excessive accumulation of asphaltene, and making the residual SBS swell again. The viscoelastic properties of the aging asphalt binder were improved by adjusting the content of components and functional groups to achieve the purpose of regeneration.