There have been many reports about the thickening ability of nanoparticles on the wormlike micelles in the recent years. Through the addition of nanoparticles, the viscosity of wormlike micelles can be increased. There still exists a doubt: can viscosity be increased further by adding more nanoparticles? To answer this issue, in this work, the effects of silica nanoparticles and temperature on the nanoparticles-enhanced wormlike micellar system (NEWMS) were studied. The typical wormlike micelles (wormlike micelles) are prepared by 50 mM cetyltrimethyl ammonium bromide (CTAB) and 60 mM sodium salicylate (NaSal). The rheological results show the increase of viscoelasticity in NEWMS by adding nanoparticles, with the increase of zero-shear viscosity and relaxation time. However, with the further increase of nanoparticles, an interesting phenomenon appears. The zero-shear viscosity and relaxation time reach the maximum and begin to decrease. The results show a slight increasing trend for the contour length of wormlike micelles by adding nanoparticles, while no obvious effect on the entanglement and mesh size. In addition, with the increase of temperature, remarkable reduction of contour length and relaxation time can be observed from the calculation. NEWMS constantly retain better viscoelasticity compared with conventional wormlike micelles without silica nanoparticles. According to the Arrhenius equation, the activation energy E_a shows the same increase trend of NEWMS. Finally, a mechanism is proposed to explain this interesting phenomenon.

Water-soluble polymers are widely used in oilfields. The rheological behaviors of these polymers in high-salinity solution are very important for stimulation of high-salinity reservoirs. In this work, a novel thermal-resistant and shear-stable amphoteric polyacrylamide (PASD), prepared from acrylamide (AM), sodium styrene sulfonate (SSS), and acryloxyethyl trimethylammonium chloride (DAC) monomers, was prepared by free-radical polymerization in high-salinity solution. The amphoteric polyacrylamide was characterized by Fourier transform infrared (FTIR) spectroscopy, nuclear magnetic resonance spectroscopy (¹H NMR), elemental analysis, thermogravimetric analysis (TG), and scanning electron microscopy (SEM). The amphoteric polyacrylamide exhibited excellent salinity tolerance. The slow increase in apparent viscosity of the polymer with increase in salinity was interesting. The amphoteric polyacrylamide showed perfect temperature resistance in high-salinity solution. The viscosity retention reached 38.9% at 120 °C and was restored to 87.8% of its initial viscosity when temperature was decreased to room temperature. The retention ratio of apparent viscosity reached 49.7% at 170 s⁻¹ and could still retain it at 25.8% at 1000 s⁻¹. All these results demonstrated that PASD had excellent thermal-resistance and shear-stability in high-salinity solution. We expect that this work could provide a new strategy to design polymers with excellent salinity-tolerance, thermal-resistance, and shear-stability performances.