While plastics are regarded as the most resourceful materials nowadays, ranging from countless utilities including protective or decorating coatings, to adhesives, packaging materials, electronic components, paintings, furniture, insulating composites, foams, building blocks and so on, their critical limitation is their advanced flammability, which in fire incidents can result in dramatic human fatalities and irreversible environmental damage. Herein, epoxy-based composites with improved flame-resistant characteristics have been prepared by incorporating two flame retardant additives into epoxy resin, namely 6-(hydroxy(phenyl)methyl)-6H-dibenzo[c,e][1,2]oxaphosphinine-6-oxide (PFR) and boric acid (H₃BO₃). The additional reaction of 9,10-dihydro-oxa-10-phosphophenanthrene-10-oxide (DOPO) to the carbonyl group of benzaldehyde yielded PFR, which was then used to prepare epoxy composites having a phosphorus content ranging from 1.5 to 4 wt%, while the boron content was 2 wt%. The structure, morphology, thermal stability and flammability of resulted epoxy composites were investigated by FTIR spectroscopy, scanning electron microscopy (SEM), thermogravimetric analysis, differential scanning calorimetry, and microscale combustion calorimetry (MCC). Thermogravimetric analysis indicated that the simultaneous incorporation of PFR and H₃BO₃ improved the thermal stability of the char residue at high temperatures. The surface morphology of the char residues, studied by SEM measurements, showed improved characteristics in the case of the samples containing both phosphorus and boron atoms. The MCC tests revealed a significant reduction in flammability as well as a significant decrease in heat release capacity for samples containing both PFR and H₃BO₃ compared to the neat epoxy thermoset.

A new method to obtain poly(vinyl chloride) (PVC) spheres, which consists of an interaction between commercial PVC grains and hexyl ethyl cellulose and lauroyl peroxide at a temperature of 60 °C, is reported. The addition of the graphene oxide (GO) sheets dispersed in dimethylformamide to the reaction mixture leads to the generation of composites made of PVC spheres coated with GO sheets. Scanning electron microscopy studies have demonstrated that this method allows for the transformation of PVC grains with sizes between 75 and 227 μm into spheres with sizes varying from 0.7 to 3.5 μm when the GO concentration in the PVC/GO composite mass increases from 0.5 to 5 wt.%. Our studies of Raman scattering and FTIR spectroscopy highlight a series of changes that indicate the appearance of ClCH=CH–, CH₂=CCl–, and/or –CH=CCl– units as a result of PVC partial dehydrogenation. New –COO– and C–OH bonds on the GO sheet surfaces are induced during the preparation of PVC spheres coated with GO sheets. A photoluminescence (PL) band with a maximum at 325 nm is reported to characterize the PVC spheres. A PVC PL quenching process is demonstrated to be induced by the increase in the concentration of the GO sheets in the PVC/GO composite mass. The perspectives regarding the use of this composite as a flame-retardant material are also reported.

In this work, new optical properties of composites based on polystyrene (PS) microspheres and graphene oxide (GO) are reported. The radical polymerization of styrene in the presence of benzoyl peroxide, pentane and GO induces the appearance of new ester groups in the PS macromolecular chains remarked through an increase in the absorbance of the infrared (IR) band at 1743 cm⁻¹. The decrease in the GO concentration in the PS/GO composites mass from 5 wt.% to 0.5 wt.% induces a diminution in the intensities of the D and G Raman bands of GO simultaneous with a down-shift of the D band from 1351 to 1322 cm⁻¹. These variations correlated with the covalent functionalization of the GO layers with PS. For the first time, the photoluminescent (PL) properties of PS/GO composites are reported. The PS microspheres are characterized by a PL band at 397 nm. Through increasing the GO sheets’ concentration in the PS/GO composite mass from 0.5 wt.% to 5 wt.%, a PS PL quenching process is reported. In addition, in the presence of ultraviolet A (UVA) light, a photo-degradation process of the PS/GO composite having the GO concentration equal to 5 wt.% is demonstrated by the PL studies.