In order to better determine the applicable working conditions of Al-Si alloy cylinder liners and cast-iron cylinder liners, their tribological performance and scuffing resistance are discussed in this paper. After wear and scuffing tests, it was found that cast-iron cylinder liners had better wear resistance and better scuffing resistance, but poor friction performance. Al-Si alloy cylinder liners had weaker wear resistance and scuffing resistance, but excellent friction performance. The wear mechanism of cast-iron cylinder liners is slight adhesive wear, and they are suitable for traditional fuel engines and turbocharged engines with high load, high power, and high stability. The wear mechanism of Al-Si alloy cylinder liners was a mixture of adhesive wear and abrasive wear, and they are suitable for engines that are lightweight, efficient, and energy-saving, and operate at high speeds.

In order to improve the wear resistance of Al-Si alloy cylinder liners, surface treatment is usually used. The Al-Si alloy cylinder liner samples were prepared by mechanical grinding and laser finishing. The mechanical grinding samples were carried out by the independent design and development of a grinding machine. The laser finishing samples were laser-heated by a CO₂ continuous transverse-flow laser. Both of the two surface treatments could provide the surfaces of protruding silicon particles with round edges to improve the wear resistance. However, in the exposure height of silicon particles with round edges, the study was lacking. The exposure height of silicon particles is important to the tribological properties of the Al-Si alloy cylinder liner, and should be analyzed in detail. The wear tests were completed by a contraposition reciprocating wear test rig under lubrication. It was found that when the silicon particles were exposed on the surface of the Al-Si alloy cylinder liner sample by 1.2 μm, the mechanical grinding samples and laser finishing samples all exhibited minimum friction coefficients and weight losses. This paper confirms that a suitable exposure height of silicon particles would reduce the probability of adhesion wear and abrasive wear of Al-Si alloy cylinder liners and increase the lubrication. It presents an excellent tribological property. However, when the exposure height of silicon particles is too high, the silicon particle is easily prone to plastic deformation or even falls off during the friction process due to the high stress and larger plastic contact index.

With the increasing demand for energy conservation and emission reduction in the automotive industry, optimizing the performance of cylinder liner and piston ring pairs in engines has become crucial. Aluminum–silicon alloy cylinder liners, known for their lightweight and excellent thermal conductivity, have emerged as a new trend in cylinder liner materials. Given the relatively moderate hardness of Al-Si alloys, judicious selection of piston rings is imperative to ensure optimal performance. This study investigates the tribological properties of aluminum–silicon alloy cylinder liners paired with CKS and DLC piston rings. The surface morphology and hardness of the test materials were characterized, and reciprocating friction and wear tests were conducted, using a tribometer to simulate operating conditions. The friction coefficient and wear volume were used as indicators to evaluate the tribological properties of the piston rings. The results show that, when the aluminum–silicon alloy cylinder liner was paired with a DLC piston ring, the friction coefficient was 27.82% lower, and the wear volume of the cylinder liner was 83.52% lower, compared to pairing with a CKS piston ring. When paired with a CKS piston ring, wear was exacerbated because silicon particles were easily dislodged to form abrasive particles. This particle detachment is mainly caused by the collision between the fine ceramic particles embedded in the CKS coating and the silicon particles (≤5 μm) uniformly distributed in the Al-Si alloy cylinder liner during the sliding process. The DLC piston ring, containing both sp² and sp³ hybridized carbon–carbon bonds, combined excellent lubrication properties with high hardness, resulting in minimal wear on both the cylinder liner and piston ring. Specifically, the DLC coating has a hardness of 2300 HV_0.3, which is 2.42 times that of the CKS piston ring (950 HV_0.3); the sp³-hybridized carbon in the DLC coating enhances its wear resistance to resist scratching from silicon particles in the cylinder liner, while the sp²-hybridized carbon forms a graphite-like transfer layer at the friction interface to reduce frictional resistance. In conclusion, the aluminum–silicon alloy cylinder liner paired with a DLC piston ring exhibits superior tribological properties. Selecting an appropriate piston ring can significantly enhance the tribological properties of the cylinder liner–piston ring pair, thereby extending the engine’s service life.