Sorption of higher concentrations of Cu(II) solution onto natural sheep wool or wool irradiated by an electron beam was studied. Sorption isotherms were of unexpected character, showing extremes. The samples with lower absorbed doses adsorbed less than non-irradiated wool, while higher doses led to increased sorption varying with both concentration and dose. FTIR spectra taken from the fibre surface and bulk were different. It was concluded that there was formation of Cu(II)-complexes of carboxylic and cysteic acids with ligands coming from various keratin macromolecules. Clusters of chains crosslinked through the ligands on the surface limit diffusion of Cu(II) into the bulk of fibre, thus decreasing the sorption. After exhausting the available ligands on the surface the remaining Cu(II) cations diffuse into the keratin bulk. Here, depending on accessibility of suitable ligands, Cu(II) creates simple or complex salts giving rise to the sorption extremes. Suggestion of a mechanism for this phenomenon is presented.

We examined the characteristics of an electron beam irradiated wool with an absorbed dose of (21–410) kGy in comparison with natural wool with respect to the determination of the isoelectric point (IEP), zero charge point (ZCP), mechanism of Cr(III) sorption from higher concentrated solutions, and the modelling of the wool-Cr(III) interaction. The data of ZPC and IEP differed between natural and irradiated samples. Increasing the dose shifted the pH of ZPC from 6.85 for natural wool to 6.20 for the highest dosed wool, while the natural wool IEP moved very little, from pH = 3.35 to 3.40 for all of the irradiated samples. The sorption experiments were performed in a pH bath set at 3.40, and the determination of the residual Cr(III) in the bath was performed by VIS spectrometry under optimized conditions. The resulting sorptivity showed a monotonically rising trend with increasing Cr(III) concentration in the bath. Lower doses, unlike higher doses, showed better sorptivity than the natural wool. FTIR data indicated the formation of complex chromite salts of carboxylates and cysteinates. Crosslinks via ligands coming from different keratin chains were predicted, preferably on the surface of the fibers, but to a degree that did not yet inhibit the diffusion of Cr(III)-cations into the fiber volume. We also present a concept of a complex octahedral structure.