Wool scoured in tap water with no special degreasing and containing a balanced humidity responding to usual laboratory conditions was irradiated by accelerated electron beam in the range of 0–350 kGy dose. Time variations of the wool structure were measured using FTIR, Raman, and EPR spectroscopy. The aim was to determine whether preexposure treatment of the wool, as well as postexposure time, affects the properties of the irradiated wool. Reactive products such as S-sulfonate, cystine monoxide, cystine dioxide, cysteic acid, disulphides, and carboxylates displayed a considerable fluctuation in quantity depending on both the absorbed dose and time. Mutual transformations of S-oxidized products into cysteic acid appeared to be faster than those in dry and degreased wool assuming that the present humidity inside the fibres is decisive as an oxygen source. EPR results indicated a longer lifetime for free radicals induced by lower doses compared with the radicals generated by higher ones. The pattern of the conformational composition of the secondary structure (α-helix,β-sheet, random, and residual conformations) also showed a large variability depending on absorbed dose as well as postexposure time. The most stable secondary structure was observed in nonirradiated wool but even this showed a small but observable change after a longer time, too.

Sorption of higher concentrations of Cu(II) solution onto natural sheep wool or wool irradiated by an electron beam was studied. Sorption isotherms were of unexpected character, showing extremes. The samples with lower absorbed doses adsorbed less than non-irradiated wool, while higher doses led to increased sorption varying with both concentration and dose. FTIR spectra taken from the fibre surface and bulk were different. It was concluded that there was formation of Cu(II)-complexes of carboxylic and cysteic acids with ligands coming from various keratin macromolecules. Clusters of chains crosslinked through the ligands on the surface limit diffusion of Cu(II) into the bulk of fibre, thus decreasing the sorption. After exhausting the available ligands on the surface the remaining Cu(II) cations diffuse into the keratin bulk. Here, depending on accessibility of suitable ligands, Cu(II) creates simple or complex salts giving rise to the sorption extremes. Suggestion of a mechanism for this phenomenon is presented.

We examined the characteristics of an electron beam irradiated wool with an absorbed dose of (21–410) kGy in comparison with natural wool with respect to the determination of the isoelectric point (IEP), zero charge point (ZCP), mechanism of Cr(III) sorption from higher concentrated solutions, and the modelling of the wool-Cr(III) interaction. The data of ZPC and IEP differed between natural and irradiated samples. Increasing the dose shifted the pH of ZPC from 6.85 for natural wool to 6.20 for the highest dosed wool, while the natural wool IEP moved very little, from pH = 3.35 to 3.40 for all of the irradiated samples. The sorption experiments were performed in a pH bath set at 3.40, and the determination of the residual Cr(III) in the bath was performed by VIS spectrometry under optimized conditions. The resulting sorptivity showed a monotonically rising trend with increasing Cr(III) concentration in the bath. Lower doses, unlike higher doses, showed better sorptivity than the natural wool. FTIR data indicated the formation of complex chromite salts of carboxylates and cysteinates. Crosslinks via ligands coming from different keratin chains were predicted, preferably on the surface of the fibers, but to a degree that did not yet inhibit the diffusion of Cr(III)-cations into the fiber volume. We also present a concept of a complex octahedral structure.

The presented review is focused on a brief overview of the scientific works on the use of sheep wool outside the textile industry that were published in recent years. The focus of the information is the on construction industry, which is a significant consumer of heat- and sound-insulating materials. With its properties, sheep wool can compete very well with insulators made from non-renewable resources. Other building elements can also be combined with wool, as long as they are used in appropriate conditions. Due to its chemical and physical structure, wool is extremely suitable for the adsorption removal of pollutants from the living and working environment, in native or modified form. Wool can also be used in recycling processes. However, each application must be preceded by an investigation of the optimal conditions of the given process, which offers researchers inspiration and interesting topics for research.

The traditional textile use of wool as a valuable renewable material needs alternative applications in order to, besides sheep milk and meat, valorize currently unnecessary wool. Each type of product containing sheep wool requires wool with customized properties. Finding suitable physical and chemical modifications needed to develop new products while minimizing harmful side effects is a challenge for scientists. The presented review provides a brief overview of works published over the last decade associated with innovative wool scouring, dyeing, antifelting, and modification of its structure without the ambition to present complete, detailed data.