The escalating global demand for polymer products and the consequent disposal challenge necessitate technological and sustainable solutions. Recent advances in the development of materials used in 3D printing equipment are described in this review, with a focus on new biocomposite materials. The investigation delves into biocomposites comprising PLA and its blends with other polymers, reinforced by plant fibers, with a particular focus on research conducted over the last five years. The information related to the raw materials’ physical, chemical, and processing properties necessary for creating biocomposite filament and printed parts were summarized. The best results in terms of tensile and flexural strength were presented and discussed, signposting future research avenues and desirable objectives. The findings elucidate that the inclusion of plant fibers led to a reduction in mechanical strength relative to pure PLA; however, when smaller particle sizes of plant fibers were added in volumes below 10%, it resulted in improved performance. Moreover, physical and/or chemical pretreatment of fibers, along with the isolation of cellulose fibrils, emerged as pivotal strategies for bolstering mechanical strengths. Noteworthy are the promising prospects presented by the incorporation of additives, while the refinement of printing parameters is key to improving the tensile and flexural strength of printed components.

Vegetable fibers are increasingly used in biocomposites, but there is a need for further development in utilizing by-products like cocoa husks. Three-dimensional printing, through Fused Filament Fabrication (FFF), is advancing rapidly and may be of great interest for applying biocomposite materials. This study focuses on developing innovative and fully biodegradable filaments for the FFF process. PLA filaments were prepared using cellulose fibers derived from cocoa husks (5% mass ratio). One set of filaments incorporated fibers from untreated husks (UCFFs), while another set utilized fibers from chemically treated husks (TCFFs). The fabricated materials were analyzed using scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and Fourier transform infrared (FTIR) techniques, and they were also tested for tensile strength. ANOVA reveals that both UCFFs and TCFFs significantly predict tensile strength, with the UCFFs demonstrating an impressive R² value of 0.9981. The optimal tensile strength for the filament test specimens was 16.05 MPa for TCFF8 and 13.58 MPa for UCFF8, utilizing the same printing parameters: 70% infill and a layer thickness of 0.10 mm. Additionally, there was an 18% improvement in the tensile strength of the printed specimens using the filaments filled with chemically treated cocoa husk fibers compared to the filaments with untreated fibers.

The growing demand for environmentally responsible lubricants motivates the use of bio-based base stocks and benign solid additives. This study assesses the tribological performance of two Amazonian vegetable oils, Carapa guianensis (andiroba) and Copaifera spp. (copaiba resin) and a paraffinic mineral oil (PNL30) formulated with different zinc oxide (ZnO) particles, namely nanocrystals and microcrystals, at 0.01, 0.05, and 0.10 wt.%. Reciprocating sliding tests, coupled with 3D profilometry, viscosity, and sedimentation analyses, were used to link dispersion stability with friction and wear responses. A preliminary stability screening constrained the practical loading window to ≤0.10 wt.% for reproducible suspensions. Performance depended on the interplay between particle type and base-oil chemistry. Andiroba exhibited the most pronounced gains, with ZnO microcrystals near 0.05 wt.% delivering the best friction outcomes and the largest wear reductions (up to ~35%). In copaiba resin oil, nanocrystals produced small, sometimes non-significant improvements, whereas microcrystals tended to worsen wear consistent with abrasive third-body effects in a less polar matrix. In PNL30, the overall benefits were modest: nanocrystal additions generally increased wear, whereas microcrystals particularly at the highest loading 0.10 wt.% achieved a 36.4% reduction in SWR, representing a measurable and statistically significant improvement in wear resistance. These results highlight that eco-efficient lubricant design should co-optimize particle characteristics and dosage with base-oil polarity and film-forming tendencies, prioritizing dispersion stability alongside tribological targets.