In this study a pulsed Nd:YAG laser was used to join Monel 400 thin foil with μm thickness. Pulse energy was varied from 1.0 to 2.25J at small increments of 0.25J. The macro and microstructures were analyzed by optical microscopy, tensile shear test and microhardness. Sound laser welds without discontinuities were obtained with 1.5J pulse energy. Results indicate that using a precise control of the pulse energy, and so a control of the bottom foil dilution rate, it is possible to weld Monel 400 thin foil. The process appeared to be very sensitive to the gap between couples

In this study a pulsed Nd:YAG laser was used to join Hastelloy C-276 thin foil with 100 microns thickness. Pulse energy was varied from 1.0 to 2.25J at small increments of 0.25J with a 4ms pulse duration. The macro and microstructures of the welds were analyzed by optical and electronic microscopy, tensile shear test and microhardness. Sound laser welds without discontinuities were obtained with 1.5J pulse energy. Results indicate that using a precise control of the pulse energy, and so a control of the dilution rate, it is possible to weld Hastelloy C-276 thin foil by pulsed Nd:YAG laser

Duplex stainless steels (DSSs), a particular category of stainless steels, are employed in all kinds of industrial applications where excellent corrosion resistance and high strength are necessary. These good properties are provided by their biphasic microstructure, consisting of ferrite and austenite in almost equal volume fractions of phases. In the present work, Nd: YAG pulsed laser dissimilar welding of UNS S32750 super duplex stainless steel (SDSS) with 316L austenitic stainless steel (ASS), with different heat inputs, was investigated. The results showed that the fusion zone microstructure observed consisted of a ferrite matrix with grain boundary austenite (GBA), Widmanstätten austenite (WA) and intragranular austenite (IA), with the same proportion of ferrite and austenite phases. Changes in the heat input (between 45, 90 and 120 J/mm) did not significantly affect the ferrite/austenite phase balance and the microhardness in the fusion zone.

The cladding process reduces manufacturing costs by depositing super austenitic stainless steel onto low-carbon steel. Arc welding techniques, especially gas tungsten arc welding (GTAW), are commonly used for this purpose. This study evaluates the influence of heat input on cladding performance. Macroscopic analysis showed good fusion of the weld beads to the base metal with no defects. Higher heat input resulted in a lower dilution rate due to increased reinforcement. A microstructural analysis of the heat-affected zones revealed similar characteristics, with martensite formation attributed to cooling conditions. Increased microhardness was observed at the interface between the cladding and base metal, corroborating the microstructural findings. Additionally, a significant enhancement in corrosion resistance was noted in the deposited layers. This research contributes to optimizing cladding processes, ensuring better material performance in industrial applications.