This study examines the impact of a dual cure activator (DCA) when applied in combination with self-adhesive resin cements on the zirconia. Sixty zirconia were prepared in compliance with the manufacturer’s directions. The specimens were randomly assigned to each group under the dark condition, following DCA and self-adhesive resin cements [RelyX universal resin cement (RXS); Maxcem elite chroma (MAC); Panavia SA cement multi (PSM)]; group 1, RXS; group 2, MAC; group 3, PSM; group 4, DCA + RXS; group 5, DCA + MAC; and group 6, DCA + PSM. The resin composite was fixed to the zirconia, surface-treated, and maintained in a dark container for 30 min. The specimens were kept in an incubator at a temperature of 37 degrees Celsius for 24 h. The universal testing device was employed to compute the shear bond strength (SBS). A stereomicroscope was used to analyze the fractured types. The data were analyzed employing the one-way ANOVA and Tukey’s test. Group 2 had the lowest SBS (4.93 ± 0.53 MPa). Group 1 (11.17 ± 0.86 MPa) and group 3 (11.48 ± 1.17 MPa) were not significantly different in SBS. Group 6 (15.61 ± 0.68 MPa) had the highest SBS but was not significantly different from group 4 (15.45 ± 1.20 MPa). The findings show that treating the zirconia surface with DCA before using the self-curing mode of self-adhesive resin cements is the best way to improve the bond between the zirconia and resin cement.

The current study evaluates the effect of morpholine on saliva-contaminated acrylic resin repaired with light-cured resin composites. Sixty rods of self-curing acrylic resin were fabricated and assigned into four groups of fifteen specimens and surface-treated with saliva, phosphoric acid (PH), morpholine (MR), liquid MMA monomer, and a universal adhesive agent (UA, Singlebond Universal) based on the following techniques: group 1, saliva; group 2, saliva + PH + MMA + UA; group 3, saliva + MMA + UA; and group 4, saliva + MR + MMA + UA. An Ultradent model was placed at the center of the specimen, and then the resin composite was pressed and light-cured for 20 s. A mechanical testing device was used to evaluate the samples’ shear bond strength (SBS) scores. The debonded specimen areas were inspected under a stereomicroscope to identify their failure mechanisms. The data were assessed by employing the one-way ANOVA approach, and the significance level (p < 0.05) was established with Tukey’s test. The greatest SBS scores for group 2 (30.46 ± 2.26 MPa) and group 4 (32.10 ± 2.72 MPa) did not differ statistically significantly from one another. The lowest SBS recorded for group 1 was 1.38 ± 0.87 MPa. All of the fractured samples in group 1 had an adhesive failure profile. Groups 2 and 4 had the greatest percentages of cohesive failures. This study concluded that applying phosphoric acid and morpholine to sandblasted self-curing acrylic resin contaminated with saliva before MMA and universal adhesive agents are applied is the most efficient protocol for stimulating SBS when it is repaired with light-cured resin composites.

This study aimed to evaluate the shear bond strengths of six self-adhesive resin cements (SACs) on porcelain surfaces and to compare the effectiveness with and without silane application. One hundred and twenty feldspathic porcelain specimens were prepared, etched with 9.5% HF, and divided into two main groups: (i) without silane, and (ii) with silane application. Each main group was further divided into six subgroups, testing six various SACs. Shear bond strength was measured using a universal testing machine, and the de-bonded surfaces were examined with a stereomicroscope. The statistical analysis was tested with two-way ANOVA and post hoc with Tukey’s. The results showed that Panavia SA Luting Multi had the highest shear bond strength, especially with silane application, while G-Cem One exhibited the lowest in the absence of silane. The addition of silane application significantly improved the shear bond strengths of G-Cem One, Panavia SA Luting Multi, and RelyX Unicem compared to situations without silane application. The adhesive and mixed failure modes were found to depend on the brand of SACs. No cohesive failure was detected. The study concludes that Panavia SA Luting Multi achieves superior shear bond strength on feldspathic porcelain when used with a separate silane agent. The etched feldspathic porcelain surface primed with silane coupling agent is recommended for optimal bond strength when using with SACs such as G-Cem One, Panavia SA Luting Multi, or RelyX Unicem.