Development of mesoporous silica nanoparticles as carriers for drug delivery systems has increased exponentially during the last decade. The present work is focused on the synthesis of silica carriers by sol–gel from tetraethyl orthosilicate (TEOS) as precursor of silica and cetyltrimethylammonium bromide (CTAB) as pore generating agent. The synthesis conditions were modified varying the molar ratio of water/TEOS, NH3/TEOS and amount of CTAB. The silica particles were characterized by scan electron microscopy techniques (FESEM), high resolution transmission electron microscopy (HR-TEM), N2 adsorption–desorption isotherms, Zeta-potential and Dynamic Light Scattering (DLS). The results show that the specific surface area and the porosity of silica particles were strongly affected by the addition of CTAB and the amount of H2O. The dispersion and stability of silica mesoporous particles is achieved in spite of the high surface reactivity. The synthesis formulation affects considerably to the particle morphology, which changes from spheres to rods when the molar ratio of H2O increases. A maximum specific surface area of 1480 m2/g was obtained with pore sizes ranging 2.5–2.8 nm

Titanium oxide-based photocatalytic filters were produced by Fused Deposition Modelling (FDM) using biopolymers obtained from renewable biomass resources. The thermoplastic route allows shaping composites through the immobilization of photoactive TiO₂ nanoparticles in an environmentally friendly bioplastic such as the polylactic acid (PLA). Composites with an inorganic charge of 30 wt% of TiO₂ nanoparticles (NPs) exhibit a 100% methyl orange (MO) degradation after 24 h of light exposition due to the extremely uniform dispersion of the nanophase within the polymer matrix in the FDM feedstock. Surface modification of TiO₂ NPs allows the optimization of the colloidal dispersion and stabilization of the inorganic charge in a PLA solution and hence, the optimal distribution of nano-photoactive points in the TiO₂/PLA filaments and scaffolds. The proposed new route of processing improves the dispersion of nano-charges comparing with the traditional thermo-pressing routes used for mixing thermoplastics based composites, avoiding the thermal degradation of the polymer and providing a customised product. In this manuscript the evolution of photodegradation with the increase of TiO₂ content in the composite and the variation of the filter geometry was evaluated.

Extensive efforts are being made to find alternative uses for lignin (LIG). In the present work the use of this biopolymer as excipient to prepare tablets was studied. For this purpose, LIG was combined with microcrystalline cellulose (MCC) and used as excipients to prepare directly compressed tablets containing a model drug, tetracycline (TC). The excipients contained different concentrations of LIG: 100%, 75%, 50%, 25% and 0% (w/w). Two different compression forces were used (two and five tonnes). When formulations were prepared using LIG as the only excipient, tablets were formed, but they showed lower densities and crushing strength than the ones obtained with only MCC or LIG/MCC blends. Moreover, tablets prepared using five tonnes of compression force showed TC releases ranging from 40% to 70% of the drug loading. On the other hand, the tablets prepared using two tonnes of compression force showed a faster and more efficient TC release, between 60% and 90%. The presence of LIG in the tablets modified significantly the release profile and the maximum amount of TC released. Finally, a DPPH (2,2-diphenyl-1-picrylhydrozyl) assay was performed to confirm that the presence of LIG provided antioxidant properties to the formulations. Accordingly, LIG has potential as a pharmaceutical excipient.