Mechanical properties are one of the most important characteristics of biomaterials for many different applications, including biomedicine. Soft biomaterials, such as hydrogels, are difficult to characterize by conventional mechanical testing, because their mechanical properties are much lower than required by conventional testing machines. In this work, we aimed to systematically study the mechanical behavior of a model soft material, polyacrylamide hydrogels, under different loading modes: tension, torsion, compression, and indentation. This allowed us to develop a comprehensive approach to the mechanical testing of soft materials. To overcome excessive compression and slippage of the hydrogel samples when fixed in the grips during tension, additional 3D-printed grips were designed. Digital image correlation was used to determine the Poisson’s ratio of the hydrogels. The Young’s modulus values obtained from all types of mechanical tests analyzed were highly correlated. However, for hydrogels with a low crosslinker concentration, 1–2%, tension–compression asymmetry was observed. Moreover, the results of the mechanical tests were verified in indentation tests, including analytical estimation, and full-scale and numerical experiments. We also discuss the limits of using a two-parameter Mooney–Rivlin model for fitting hydrogel uniaxial tension deformation curves, which was unstable for the hydrogels with 4 and 9% crosslinker concentration. The implemented approach provided a comprehensive analysis of the mechanical behavior of biomaterials. The elastic moduli for all hydrogels studied were in the range from 20 to 160 kPa, which corresponds well to human soft tissues, making them a promising material for application as tissue-mimicking phantoms.

The purpose of this work is to theoretically and experimentally investigate the applicability of the Tsai–Hill failure criterion and classical laminate theory for predicting the strength and stiffness of 3D-printed polylactide laminate composites with various raster angles in mechanical tests for uniaxial tension and compression. According to the results of tensile and compression tests, the stiffness matrix components of the orthotropic individual lamina and strength were determined. The Poisson’s ratio was determined using the digital image correlation method. It was found that the Tsai–Hill criterion is applicable for predicting the tensile strength and yield strength of laminate polymer composite materials manufactured via fused deposition modeling 3D printing. The calculated values of the elastic moduli for specimens with various raster angles correlate well with the values obtained experimentally. In tensile tests, the error for the laminate with a constant raster angle was 3.3%, for a composite laminate it was 4.4, in compression tests it was 11.9% and 9%, respectively.

Objective and Design: The search for improved stenting technologies to treat peripheral artery disease is trending toward biodegradable self-expanding shape-memory stents that, as of now, still suffer from the acute trade-off between deliverability and luminal stability: Higher deliverability leads to lower lumen stability, vessel recoil, and stent breakage. This study was aimed at the development and testing of a self-expanding bioresorbable poly(l,l-lactide-co-ε-caprolactone) stent that was designed to produce confident self-expansion after efficient crimping, as well as quick bioresorption, and sufficient radial force. Materials and Methods: Bench tests were employed to measure shape-memory properties, radial force, and hydrolytic degradation of the stent. The porcine model was employed to study deliverability, lumen stability, biocompatibility, and stent integrity. A total of 32 stents were implanted in the iliac arteries of 16 pigs with 15 to 180 day follow-up periods. The stented vessels were studied by angiography and histological evaluation. Results: Recovery of the diameter of the stent due to shape-memory effect was equal to 90.6% after 6Fr crimping and storage in refrigeration for 1 week. Radial force measured after storage was equal to 0.7 N/mm. Technical success of implantation in pigs (after the delivery implemented by pusher) was 94%. At 180 days, no implanted stents were found to be fragmented: All of the devices remained at the site of implantation with no stent migration and all stents retained their luminal support. Only moderate inflammation and neoepithelialization were detected by histological assessment at 60, 90, 120, and 180 days. Lumen loss at 180 days was less than 25% of the vessel diameter. Conclusions: The stent with the mechanical and chemical properties described in this study may present the optimal solution of the trade-off between deliverability and luminal stability that is necessary for designing the next generation stent for endovascular therapy of peripheral arterial disease.

A comparative analysis of the microstructure and mechanical properties of guided bone regeneration frame membranes made from Ti6Al4V titanium alloy powder using 3D printing technology is presented in this paper. Two different methods were used to produce the samples: direct laser sintering of metals (DMLS) and electron beam melting (EBM). The plates, measuring 30×10×1 mm, were formed from layers 30 µm thick. The surface morphology of the samples was studied at both the micro and macro levels using scanning electron microscopy (SEM) and scanning impulse acoustic microscopy (SIAM). Biocompatibility was assessed both in vitro with mesenchymal stem cell (MSC) cultures and in vivo with laboratory animals. Mechanical properties were evaluated using a three-point bending test, which revealed differences in surface profile depth that was 100 and 150 µm for the DMLS and EBM correspondingly. Samples produced using DMLS technology demonstrated higher strength 2,180±20.7 MPa and elasticity 53,449±200 MPa than those produced by EBM strength 1500±26.1 and elasticity 25,633±125 MPa, according to the results of the mechanical tests. A more active proliferation of MSCs was observed in vitro in the DMLS samples, which was 70% higher compared to EMB and the control group. The bone tissue response to both types of titanium implants was good, with high levels of osseointegration, as confirmed by X-ray microtomography (µCT).