We evaluated the strength and durability characteristics of latex-polymer-modified, pre-packed pavement repair concrete (LMPPRC) with a rapid-set binder. The rapid-set binder was a mixture of rapid-set cement and silica sand, where the fluidity was controlled using a latex polymer. The resulting mix exhibited a compressive strength of ¥21 MPa and a flexural strength of ¥3.5 MPa after 4 h of curing (i.e., the traffic opening term for emergency repairs of pavement). The ratio of latex polymer to rapid-set binder material was varied through 0.40, 0.33, 0.29, and 0.25. Mechanical characterization revealed that the mechanical performance, permeability, and impact resistance increased as the ratio of latex polymer to rapid-set binder decreased. The mixture exhibited a compressive strength of ¥21 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ¤0.29. The mixture exhibited a flexural strength of ¥3.5 MPa after 4 h when the ratio of latex polymer to rapid-set binder material was ¤0.33. The permeability resistance to chloride ions satisfied 2000 C after 7 days of curing for all ratios. The ratio of latex polymer to rapid-set binder material that satisfied all conditions for emergency pavement repair was ¤0.29.

Various studies have been conducted to minimize the damage and loss of stored grain. For safe storage, the moisture content must be reduced, or respiration must be suppressed. In this study, grain respiration rates were analyzed under various nitrogen atmospheric conditions, and the quality of stored rice was evaluated. As the nitrogen content of the storage space increases, the respiration rate of the grain decreases accordingly. In this study, the effect of the modified atmospheric nitrogen concentration on reducing respiration was determined. When predicting weight loss due to respiration, low moisture content, and high nitrogen concentration could reduce loss. Quality analysis was performed to compare different respiration rate conditions and showed that lower oxygen concentration and moisture content were associated with safer storage. Our results indicate that changes in atmospheric conditions depending on climate and storage conditions can be considered for the safe storage of harvested rice.