Bearing steel (GCr15) is widely used in key parts of mechanical transmission for its excellent mechanical properties. Electrochemical machining (ECM) is a potential method for machining GCr15, as the machining process is the electrochemical dissolution of GCr15 regardless of its high hardness (>50 HRC). In ECM, NaNO₃ solution is a popular electrolyte, as it has the ability to help in the nonlinear dissolution of many metallic alloy materials, making it useful for precision machining. However, due to high carbon content of GCr15, the electrochemical dissolution of GCr15 is unique, and there is always a black layer with high roughness on the machined surface, reducing the surface quality. In order to improve the electrochemical machining of GCr15 with a high surface quality, the surface characteristics of GCr15 in ECM were investigated. The anodic polarisation curve in the NaNO₃ electrolyte was measured and electrochemical dissolution experiments were conducted with different current densities. SEM, XRD, and XPS were employed to analyse the surface morphology and composition formed on the machined surface at different current densities. The initial results showed that there were two parts (black part and bright part) formed on the machined surface when a short circuit occurred, and the test results suggested that the black part contained a mass of Fe₃O₄ while the bright part was composed of mainly Fe and Fe₃C. Further investigation uncovered that a black flocculent layer (Fe₃O₄) always formed in a low current density (32 A/cm²) with high roughness. With the current density increased, the amount of black flocculent layer was reduced, and Fe₃C particles appeared on the machined surface. When the current density reached 81 A/cm², the entire flocculent oxide layer was removed, only some spherical Fe₃C particles were inserted on the machined surface, and the roughness was reduced from Ra7.743 μm to Ra1.783 μm. In addition, due to exposed Fe₃C particles on the machined surface, the corrosion resistance of the machined surface was significantly improved. Finally, circular arc grooves of high quality were well manufactured with current density of 81 A/cm² in NaNO₃ electrolyte.

Multi-channel high-speed wire electrical discharge machining (HSWEDM) has shown great potential in enhancing the cutting rate of metal workpieces. However, the mechanism of multi-channel discharges in this technique remains unclear. In this paper, the equivalent circuit and processing model of the multi-channel HSWEDM were developed to investigate the discharge characteristics. It was found that the equipotential between electrodes is the primary factor causing electrical signal coupling between channels, hindering the achievement of synchronous discharge. To address this issue, a novel power supply with a decoupling circuit was devised. By utilizing the combined effect of electrode wire resistance and current limiting resistance (R_c), a potential difference was induced between electrodes in different channels, enabling electrical signal decoupling and facilitating synchronous discharge. The impact of R_c on synchronous discharge was examined, revealing that a reduction in R_c can increase the gap voltage of non-breakdown channels, thereby enhancing the discharge ratio. Finally, cutting rate experiments were conducted. When the new power supply was used for electrical signal decoupling, the cutting rates of multi-channel WEDM were significantly improved. Compared to single-channel HSWEDM, the cutting rates of two-channel and four-channel HSWEDM are enhanced by 84.06% and 247.83%, respectively.