The dynamically developing field of implantology requires researchers to search for new materials and solutions. In this study, TiNbZr samples were investigated as an alternative for popular, but potentially hazardous TiAl6V4. Samples were etched, sandblasted, subjected to PEO, and covered in AgNP suspension. Simultaneously, SEM images were taken, and the wettability and roughness of the surface were measured. Samples covered in AgNPs were subjected to biological trials. A six-day measurement of human fibroblast proliferation was conducted to assess biocompatibility, and the population of E. coli and S. aureus was measured over eight hours. Results showed that the TiNbZr PEO surface is biocompatible with human fibroblast cells and promotes growth. However, deposited AgNPs exhibited only slight effectiveness in decreasing bacterial growth over the first two hours. The results suggest that the method of surface preparation is sufficient and might promote osseointegration. On the other hand, more efficient and reliable methods of application of AgNPs should be researched

The increased demand for implants that do not pose a threat to patients diagnosed using high-resolution magnetic resonance imaging and concerns arising from titanium allergies require the development of alternative implant materials. One promising concept is a use of zirconium as corrosion-resistant, nontoxic material that is lower in magnetic susceptibility. To achieve this, safe and efficient surface treatment methods of zirconium metal have to be developed. In this study, zirconium samples were treated with fluoride-free and fluoride-containing etching mixtures to determine their effect on the surface of Zr. SEM images were taken to investigate the preliminary effects of the etchants. Then, a second set of experiments was carried out using mixtures of HF-H₂SO₄ and ammonium persulfate–fluoride salts, as they gave the most promising results in the first trial. SEM images were taken and measurements on roughness, wettability, and atomic composition were made. The results showed an even zirconium surface in APS-fluoride salts, along with the formation of pits (1–3 μm) similar to those found in commercially available implants. There was no significant increase in the roughness of the treated samples. The addition of NO₃⁻ ions in the form of KNO₃ speeded up etching and promoted pit formation. The HF-H₂SO₄ mixture was found to give unsatisfying results, as the surface was too rough and the formed pits were too large. It was concluded that etching zirconium in ammonium persulfate and fluoride salts is a promising area of research for the preparation of zirconium implants; however, further research has to be carried out on sandblasted samples.