Underwater artefacts are vulnerable to damage and loss of archaeological information during the extraction process. To solve this problem, it is necessary to apply temporary consolidation materials to fix the position of marine artifacts. A cross-linked network hydrogel composed of polyvinyl alcohol (PVA), tannic acid (TA), borax, and calcium chloride has been created. Four hydrogels with varying concentrations of tannic acid were selected to evaluate the effect. The hydrogel exhibited exceptional strength, high adhesion, easy removal, and minimal residue. The PVA/TA hydrogel and epoxy resin were combined to extract waterlogged wooden artifacts and marine archaeological ceramics from a 0.4 m deep tank. This experiment demonstrates the feasibility of using hydrogel for the extraction of marine artifacts.

A comprehensive multi-analytical investigation was conducted on a piece of Longquan celadon excavated from the Shengbeiyu shipwreck site in the East China Sea. This study focused on a representative type of tubular bio-concretions attached to the submerged celadon, believed to have been formed through the construction activities of a marine tubeworm belonging to the benthic phylum of Polychaeta Annelids. The research examined the microstructure, composition and adhesion form of these tubular bio-concretions, aiming to elucidate their developmental and attachment patterns from a biomineralization and biofouling perspective. The tubular bio-concretions were found to have a bimineralic composition, with notably higher content of aragonite than calcite, and display diverse yet highly ordered microstructures. The presence of organic matter within the bio-concretions indicates an organic matrix-controlled crystallization model, commonly observed in the construction of benthic calcareous tubes. Microscopic analyses revealed the primary degradation microstructures and corresponding phases of the glaze to which calcareous tubes attached. These findings closely resembled the corrosion characteristics observed in submerged ceramic glaze without bio-concretion attachments, as documented in earlier studies. OM and SEM observations also indicated that the calcareous tubes intricately intermeshed with the cracked glaze layer of the celadon. Additionally, Raman spectroscopic analysis detected the presence of proteins at the interface, likely residual adhesives secreted by fouling organisms to cement themselves to the settlement substrata, suggesting the occurrence of organic-mediated bio-adhesion mechanisms. These results shed new light on the formation process of bio-concretions and their interaction with attached underwater ceramics. A simplified formation mechanism of this biologically-induced degradation has been discussed.

The use of epoxy resin/carbon fiber multilayer materials can effectively prevent damage to artifacts during underwater archaeological artifact extraction. However, the high viscosity of epoxy resin limits the coating ability and curing quality. To solve this problem, propylene carbonate (PC) was used as a diluent to reduce the viscosity and improve the properties. This study investigated the gel time, curing time, curing degree, and mechanical strength of the cured products by varying PC concentrations. It was found that the PC significantly enhanced the flowability of epoxy resin blends, extending the gel time from 22 min to 38 min, with minimal impact on the curing time. The glass transition temperature (Tg) ranged from 25.80 °C to 12.28 °C. Compared to E44/PC0, PC reduced the CTE values in the weft direction. The multilayer materials exhibited good temperature stability. The cured product had good mechanical properties and toughness, and could wrap irregular artifacts. The E44/PC10 formulation was used to prepare the epoxy resin/carbon fiber multilayer material. Waterlogged wooden artifacts were successfully extracted from 13 m deep calm water, using the multilayer material.

Block lifting is a key step in stabilizing and removing fragile remains at archaeological excavation sites. Due to its favorable working properties and adhesive effect, menthol has recently been proposed as a volatile binding medium for temporary consolidation in archaeological conservation. This paper presents a case study on the use of menthol in the extraction and restoration of a large wooden coffin lid, approximately 1.9 m long and 0.9 m wide, from tomb 11 (M11) at Xie’ertala, located east of a Xie’ertala town in Hailar City, Inner Mongolia, dating to the 7th to 10th centuries CE. This coffin lid had fragmented into numerous wooden pieces, and was preserved in a relatively arid steppe environment, necessitating the extraction of the lid as a consolidated block. The use of menthol for consolidating and lifting the highly fragmented wooden coffin lid was intended to preserve critical archaeological information while avoiding damage to the underlying objects. An analysis of the physicochemical properties of these wooden remains suggests that the timber used for the coffin lid belongs to a common pine species from the Hulunbuir region. The degradation of the coffin lid was relatively mild, as shown by Fourier Transform Infrared Spectroscopy (FT-IR) and Scanning Electron Microscope (SEM) results. Dynamic Vapor Sorption (DVS) tests indicated that the hygroscopicity of the archaeological wood was 23.4%, compared to 21.1% for the reference sample, demonstrating good environmental stability. The safety of menthol as a treatment for fragile wooden remains was evaluated by comparing changes in the morphological and porosity characteristics of the coffin lid before and after menthol treatment. After treatment, the widths of the fissures remained largely unchanged, with all relative variations being less than 1%, and the porosity as well as pore size distribution of the wood showed negligible changes. Gas Chromatography–Mass Spectrometry (GC-MS) results showed that only 0.6% of menthol residue remained after 8 days of sublimation. This pilot study demonstrates that menthol is a safe temporary consolidant for block lifting and offers a promising alternative to the widely used cyclododecane. In conclusion, this research provided a new approach for conservators to safely lift similarly large and fragile wood remains during archaeological excavations.