The molecular dynamics, with an emphasis on the calorimetric and dynamic glass transitions, of non-isocyanate polyhydroxyurethanes (PHUs) produced by the equimolar polyaddition of polyether-based dicyclic carbonates (P-CCs) and various short diamines was studied. The diamine component consisted of a short aliphatic diamine (1,4-diaminobutane, DAB) and a more complex ‘characteristic’ diamine. The study was conducted to investigate (i) the chemical structure of the characteristic amine, (ii) its molar ratio, and (iii) the structure and molar mass of the P-CC. Infrared spectroscopy, differential scanning calorimetry, and broadband dielectric spectroscopy were employed. The P-CC, constituting the bulk of the systems, was the most crucial component for the glass transition. The characteristic amine influenced the glass transition as a result of its bulky structure, but also presumably as a result of the introduction of free volume and the formation of hydrogen bonds. The dynamic glass transition (α relaxation) trace in the Arrhenius plots showed a subtle change at a certain temperature that merits further study in the future. The charge mobility was fully coupled with the molecular mobility, as evidenced by dc conductivity being directly proportional to the characteristic frequency of α relaxation. The fluctuation in carbonyl units (β relaxation) was mildly affected by changes in their immediate environment.

In this work, we report on flexible toluene diisocyanate (TDI)-based polyurethane foams (FPUFs) chemically modified by POSS moieties, i.e., octa (3-hydroxy-3-methylbutyldimethylsiloxy) POSS (OCTA-POSS) and 1,2-propanediolizo-butyl POSS (PHI-POSS). The influence of silsesquioxane on the PU foaming process, structure, morphology, physicochemical, and mechanical properties, as well as flammability, was examined. FT-IR analysis provided evidence for the chemical incorporation of the nanofiller into the foam structure. It was found that the addition of POSS increases the apparent density of the foam and its compressive strength. The XRD and SEM-EDS techniques showed the uniform distribution of POSS in the FPUF with agglomeration depending on the kind and content of the introduced POSS moieties. The analysis of the thermogravimetric and microcalorimetry data revealed an improved resistance to the burning of FPUFs containing reactive POSS, as evidenced by the reduced rate of heat release (HRR). Importantly, the mechanical properties tests showed that the incorporation of silsesquioxane nanoparticles into the polyurethane structure via covalent bonds strengthens the foam integrity.

Non-isocyanate polyurethane (NIPU) networks physically modified with octa(3-hydroxy-3-methylbutyldimethylsiloxy)POSS (8OHPOSS, 0–10 wt%) were conditioned in environments of different relative humidities (up to 97%) to study water–polymer interactions. The equilibrium sorption isotherms are of Brunauer type III in a water activity range of 0–0.97 and are discussed in terms of the Guggenheim (GAB) sorption model. The study shows that the introduction of 8OHPOSS, even in a large amount (10 wt%), does not hinder the water affinity of the NIPU network despite the hydrophobic nature of POSS; this is attributable to the homogenous dispersion of POSS in the polymer matrix. The shift in the urethane-derived carbonyl bands toward lower wavenumbers with a simultaneous shift in the urethane N-H bending bands toward higher wavenumbers exposes the breakage of polymer–polymer hydrogen bonds upon water uptake due to the formation of stronger water–polymer hydrogen bonds. Upon water absorption, a notable decrease in the glass transition temperature ($T_g$) is observed for all studied materials. The progressive reduction in $T_g$ with water uptake is driven by plasticization and slaving mechanisms. POSS moieties are thought to impact slaving indirectly by slightly affecting water uptake at very high hydration levels.