Investigations into the surface modification of a Ti-15Mo alloy via plasma electrolytic oxidation are reported. The oxidation process was conducted in a solution containing Ca(H2PO2)2, H 3PO4, or (HCOO)2Ca. Anodisation was performed at voltages in the range of 100-400 V. The morphology of the sample surface did not change during alloy oxidation at lower voltages. Higher voltages led to the incorporation of calcium and phosphorus or of calcium only into the formed oxide layer and to significant modification of the surface morphology. Based on the SEM and EDX analysis results, a set of samples was selected for further investigations. To study the surface of the Ti-Mo alloy after anodic oxidation, we used scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), thin-layer X-ray diffraction (TL-XRD), and X-ray photoelectron spectroscopy (XPS). The electrochemical characteristics of the modified alloy in Ringer's solution were determined. Anodisation results in a considerable increase in the corrosion resistance of the Ti-15Mo alloy. © 2013 Elsevier Ltd

The biodegradable metals, including magnesium (Mg), are a convenient alternative to permanent metals but fast uncontrolled corrosion limited wide clinical application. Formation of a barrier coating on Mg alloys could be a successful strategy for the production of a stable external layer that prevents fast corrosion. Our research was aimed to develop an Mg stable oxide coating using plasma electrolytic oxidation (PEO) in silicate-based solutions. 99.9% pure Mg alloy was anodized in electrolytes contained mixtures of sodium silicate and sodium fluoride, calcium hydroxide and sodium hydroxide. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), contact angle (CA), Photoluminescence analysis and immersion tests were performed to assess structural and long-term corrosion properties of the new coating. Biocompatibility and antibacterial potential of the new coating were evaluated using U2OS cell culture and the gram-positive Staphylococcus aureus (S. aureus, strain B 918). PEO provided the formation of a porous oxide layer with relatively high roughness. It was shown that Ca(OH)₂ was a crucial compound for oxidation and surface modification of Mg implants, treated with the PEO method. The addition of Ca²⁺ ions resulted in more intense oxidation of the Mg surface and growth of the oxide layer with a higher active surface area. Cell culture experiments demonstrated appropriate cell adhesion to all investigated coatings with a significantly better proliferation rate for the samples treated in Ca(OH)₂-containing electrolyte. In contrast, NaOH-based electrolyte provided more relevant antibacterial effects but did not support cell proliferation. In conclusion, it should be noted that PEO of Mg alloy in silicate baths containing Ca(OH)₂ provided the formation of stable biocompatible oxide coatings that could be used in the development of commercial degradable implants.

Plasma electrolytic oxidation (PEO) can provide an ideal surface for osteogenic cell attachment and proliferation with further successful osteointegration. However, the same surface is attractive for bacteria due to similar mechanisms of adhesion in prokaryotic and eukaryotic cells. This issue requires the application of additional surface treatments for effective prevention of postoperative infectious complications. In the present work, ZrNb alloy was treated in a Ca-P solution with Ag nanoparticles (AgNPs) for the development of a new oxide layer that hosted osteogenic cells and prevented bacterial adhesion. For the PEO, 0.5 M Ca(H₂PO₂)₂ solution with 264 mg L⁻¹ of round-shaped AgNPs was used. Scanning electron microscopy with energy-dispersive x-ray and x-ray photoelectron spectroscopy were used for morphology and chemical analysis of the obtained samples; the SBF immersion test, bacteria adhesion test, and osteoblast cell culture were used for biological investigation. PEO in a Ca-P bath with AgNPs provides the formation of a mesoporous oxide layer that supports osteoblast cell adhesion and proliferation. Additionally, the obtained surface with incorporated Ag prevents bacterial adhesion in the first 6 h after immersion in a pathogen suspension, which can be an effective approach to prevent infectious complications after implantation.