Investigations into the surface modification of a Ti-15Mo alloy via plasma electrolytic oxidation are reported. The oxidation process was conducted in a solution containing Ca(H2PO2)2, H 3PO4, or (HCOO)2Ca. Anodisation was performed at voltages in the range of 100-400 V. The morphology of the sample surface did not change during alloy oxidation at lower voltages. Higher voltages led to the incorporation of calcium and phosphorus or of calcium only into the formed oxide layer and to significant modification of the surface morphology. Based on the SEM and EDX analysis results, a set of samples was selected for further investigations. To study the surface of the Ti-Mo alloy after anodic oxidation, we used scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), thin-layer X-ray diffraction (TL-XRD), and X-ray photoelectron spectroscopy (XPS). The electrochemical characteristics of the modified alloy in Ringer's solution were determined. Anodisation results in a considerable increase in the corrosion resistance of the Ti-15Mo alloy. © 2013 Elsevier Ltd

Total Productive Maintenance (TPM) is an infrastructure-managing methodology that leads to improvements in production efficiency, quality, and safety. It includes a set of processes, techniques, and strategies based on forecasting, maintenance, the optimized cooperation of different company departments, and the minimization of costs related to downtime or accidents caused by equipment failure. This article discusses the history, assumptions of the TPM concept, and approach to implementing Total Productive Maintenance in organizations in detail. The right ingredients required for successful TPM implementation and barriers to implementation are also reviewed. The benefits of implementing TPM in organizations are presented and supported with examples of implementations in production and non-production organizations. The article is addressed to representatives of the manufacturing industry. TPM also indicates a high potential for implementation in non-production areas, which may be interesting, for example, for the service, medical, or laboratory industries.

The electronic components mounted on the printed circuit boards (PCBs) of mobile phones represent a resource that is rich in metals, and after separation from the boards, these components could be considered secondary raw materials. The concentrations of the valuable metals are insignificant when compared with those of complete PCBs; however, they could be significantly higher in a fraction formed from the separated components. This study focused on the analysis of Ag, Au, Cu, Nd, Nb, Ni, Pb, Pd, Sn, and Ta in fractions produced by the separation of all the components mounted on PCBs from several types of mobile phones. Atomic absorption spectrometry, atomic emission spectrometry, and mass spectrometry techniques were utilized, and a comparison of five older models of “brick” phones and five modern smartphones was conducted. Additionally, 50 kg of PCBs from the current recycling market were analyzed in the same way to create a summary of the current recycling stream.

According to the idea of sustainable development, humanity should make every effort to care for the natural environment along with economic development. Decreasing water resources in the world makes it necessary to take action to reduce the consumption of this resource. This article presents the results of research conducted to improve the use of recyclable materials in line with the circular economy model. The research focused on the development of a technological solution for the recovery of raw materials from galvanic wastewater. The concept of a galvanic wastewater treatment system presented in the article includes wastewater pre-treatment in the ultrafiltration (UF) process and water recovery in the reverse osmosis (RO) process. In addition, the purpose of the work was to manage post-filtration waste (RO retentate) containing high concentrations of zinc in the process of galvanizing metal details. The obtained results indicate that it is possible to reduce the amount of sewage from the galvanizing industry by reusing the recovered water as technical water in the process line. The carried-out model tests of galvanizing confirmed the possibility of using RO retentate for the production of metal parts. The achieved results are a proposal to solve the problem of reducing the impact of galvanic wastewater on the environment and to improve the profitability of existing galvanizing technologies by reducing the consumption of water and raw materials.