A novel ultrathin g-C₃N₄ nanosheet-modified BiOCl hierarchical flower-like plate heterostructure (abbreviated as BC/CN) was constructed via a thermal polymerization of urea precursor followed with hydrolysis route. The as-prepared samples were well characterized by various analytical techniques. The morphological observation showed that hierarchical flower-like BiOCl nanoplates were discretely anchored on the surface of ultra-thin C₃N₄ nanosheets. The photocatalytic performance of the as-prepared photocatalysts was evaluated by degradation of methylene blue (MB) under visible-light irradiation. The results showed that BC/CN photocatalyst exhibited enhanced photostability and photocatalytic performance in the degradation process. On the basis of experimental results and the analysis of band energy structure, it could be inferred that the enhanced photocatalytic performance of BC/CN photocatalyst was intimately related with the hybridization of hierarchical flower-like BiOCl nanoplates with ultrathin g-C₃N₄ nanosheets, which provided good adsorptive capacity, extended light absorption, suppressed the recombination of photo-generated electron–hole pairs, and facilitated charge transfer efficiently.

Impurity element doping is extensively taken as one of the most efficient strategies to regulate the electronic structure as well as the rate of photogenerated charge separation of photocatalysts. Herein, a one-pot hydrothermal synthesis process was exploited to obtain La-doped ZnIn₂S₄ microspheres, aiming at gaining insight into the role that doping ions played in the improvement of pollutant photodegradation. Systematical characterization means, comprising of X–ray photoelectron spectroscopy (XPS), ultraviolet–visible (UV–vis) diffuse reflection spectroscopy and Raman spectra, combination with high-resolution transmission electron microscopy (HRTEM), were employed to in depth reveal the concomitancy of La ions and ZnIn₂S₄ crystal lattice. The results showed that the La-doped ZnIn₂S₄ samples exhibited a slightly wider and stronger spectral absorption than pristine ZnIn₂S₄; and the specific surface area of doped ZnIn₂S₄ samples was a bit larger. The La-doped ZnIn₂S₄ electrodes showed improved photocurrent response, and the photocurrent density reached a maximum value at La content of 1.5 wt%. As expected, La-doped ZnIn₂S₄ samples exhibited a remarkable enhancement of photocatalytic behaviour toward the photodegradation of tetracycline hydrochloride (TCH) and methyl orange (MO). The prominently enhanced photoactivity of doped ZnIn₂S₄ samples was due to the synergistic effect of the elevated visible-light absorption ability and effective photogenerated charge carriers’ separation.

Regardless of its good electron-transfer ability and chemical stability, pure Zn₂SnO₄ (ZSO) still has intrinsic deficiencies of a narrow spectral response region, poor absorption ability, and high photo-activated carrier recombination rate. Aiming to overcome the deficiencies above-mentioned, we designed a facile hydrothermal route for etching ZSO nanoparticles in a dilute acetic acid solution, through which efficient oxygen vacancy defect engineering was accomplished and SnO_2−x nanocrystals were obtained with an ultrafine particle size. In comparison with the untreated ZSO nanoparticles, the specific surface area of SnO_2−x nanocrystals was substantially enlarged, subsequently leading to the notable augmentation of active sites for the photo-degradation reaction. Aside from the above, it is worth noting that SnO_2−x nanocrystals were endowed with a broad spectral response, enhancing light absorption capacity and the photo-activated carrier transfer rate with the aid of oxygen vacancy defect engineering. Accordingly, SnO_2−x nanocrystals exhibited significantly enhanced photoactivity toward the degradation of the organic dye rhodamine B (RhB), which could be imputed to the synergistic effect of increasing active sites, intensified visible-light harvesting, and the separation rate of the photo-activated charge carrier caused by the oxygen vacancy defect engineering. In addition, these findings will inspire us to open up a novel pathway to design and prepare oxide compound photocatalysts modified by oxygen vacancy defects in pursuing excellent visible-light photoactivity.

Improving the photocatalytic performance of multi-component photocatalysts through structural modulation and band alignment engineering has attracted great interest in the context of solar energy utilization and conversion. In our work, Zn₂SnO₄/SnO₂ hierarchical architectures comprising nanorod building block assemblies were first achieved via a facile solvothermal synthesis route with lysine and ethylenediamine (EDA) as directing agents, and then chemically etched in NaOH solution to enlarge the surface area and augment active sites. The etched Zn₂SnO₄/SnO₂ hierarchical architectures were further decorated by Cu₂O nanoparticles though an in situ chemical deposition method based on band alignment engineering. In comparison with unetched Zn₂SnO₄/SnO₂, the specific surface area of Zn₂SnO₄/SnO₂/Cu₂O hierarchical architectures became larger, and the responsive region and absorbance intensity became wider and higher in the whole visible-light range. Zn₂SnO₄/SnO₂/Cu₂O hybrid photocatalysts presented enormously improved visible-light photocatalytic behaviour for Rhodamine B (RhB) decomposition. The enhancement of photocatalytic behaviour was dominantly attributed to the synergy effect of the larger specific surface area, higher light absorption capacity, and more effective photo-induced charge carrier separation and migration. A proposed mechanism for the enormously promoted photocatalytic behaviour is brought forth on the basis of the energy-band structure combined with experimental results.