Severe hot tearing has been observed during DC casting of modified AA3000 alloys with additions of Cu, Ti, and Zr, although these alloys are regarded as rather easy to cast. Extensive studies have been performed on both synthetic and industrial AA2000, AA6000, and AA7000 alloys, but less data are available for AA3000 alloys. This work was thus initiated to investigate the hot tearing susceptibility of AA3000 alloys with varying alloy element content using constrained rod casting molds. The results showed that the Cu and Fe content have a major impact on hot tearing resistance, while the effects of Zr and Ti are minor. Cu in a range from 0.3 to 1.2 wt pct significantly increased the hot tearing tendency. This is due to the existence of high eutectic fractions at low temperatures, as well as porosity formation associated with bad feeding at the end of solidification. A strong cracking tendency was observed below an Fe content 0.2 wt pct owing to decreased precipitation of the Al₆(Mn, Fe) phase. It was found that primary Al₆(Mn, Fe) phases lead to early bridging between the grains, which reinforces the alloy during the vulnerable temperature range for hot tearing. Zr and Ti additions weakly enhanced or reduced hot tearing severity, respectively.

Considerable research has been devoted to the development of cathode materials for Al-ion batteries, but challenges remain regarding the behavior of aluminum anodes. Inert oxide (Al₂O₃) film on Al surfaces presents a barrier to electrochemical activity. The structure of the oxide film needs to be weakened to facilitate ion transfer during electrochemical activity. This study addresses oxide film challenges by studying Al alloy anodes with different iron content. The results reveal that using an anode of 99% Al 1% Fe in a cell increases the cycling lifetime by 48%, compared to a 99.99% Al anode. The improvement observed with the 99% Al 1% Fe anode is attributed to its fractional surface area corrosion being about 12% larger than that of a 99.99% Al anode. This is coupled to precipitation of a higher number of Al₃Fe particles, which are evenly scattered in the Al matrix of 99% Al 1% Fe. These Al₃Fe particles constitute weak spots in the oxide film for the electrolyte to attack, and access to fresh Al. The addition of iron to an Al anode thus offers a cheap and easy route for targeting the oxide passivating film challenge in Al-ion batteries.