Expansive or soft soils cause significant geotechnical issues for foundations and subgrades because they show swell–shrink behaviour under wet and dry conditions. These volume changes can result in cracking, heaving, uneven settlement, and structural or pavement damage, ultimately increasing maintenance and repair costs. While traditional Portland cement and lime stabilisers effectively enhance soil strength and reduce swell–shrink behaviour, the cement production process is responsible for only approximately 7%–8% of global CO₂ emissions, prompting a transition toward sustainable alternatives. This comprehensive review consolidates recent advancements in soil stabilisation using industrial by-products, such as fly ash, ground granulated blast furnace slag (GGBS), steel slag, cement kiln dust, silica fume, bottom ash, red mud, waste foundry sand, brick dust, calcium carbide residue, water treatment sludge, etc. These materials leverage pozzolanic and latent hydraulic properties to form C-A-H, C-S-H, and N-A-S-H gels, thereby densifying the soil microstructure, improving CBR (%), UCS, and reducing plasticity and swelling potential. Optimisation studies indicate that industrial waste stabilisers often match or exceed conventional binder performance, GGBS-steel slag combinations yielding 105% higher UCS than ordinary Portland cement, and silica fume enhances cement-stabilised soils by 22% at reduced dosages. However, inherent compositional variability, long-term durability concerns including sulfate attack and freeze–thaw degradation, and the absence of standardised design guidelines restrict large-scale implementation. This review integrates mechanistic, microstructural, and sustainability insights, highlighting the need for durability research, standardised methods, and large-scale field validation to advance industrial waste-based stabilisation within circular construction practices in geotechnical engineering.

This study evaluated the effect of alum sludge as an alternative to fly ash in fabricating geopolymer paste and mortar. The blending of this industrial waste (alum sludge and fly ash) is not only for the benefit of sustainable construction and disposal of industrial waste but also for the reduction of CO₂ emissions due to the increasing production of Portland cement from the cement production industry. A laboratory investigation was carried out on the workability and mechanical properties of geopolymer paste and mortar produced with alum sludge replacement in different proportions (0, 10, 20, 30, 40, 50, 60, 70, 80, 90, and 100). A combination of an alkaline solution of sodium silicate and sodium hydroxide of 14 molarity was employed as an activator for the manufacturing of both paste and mortar geopolymer specimens. It was observed from the findings that geopolymer paste and mortar was flowable and workable when alum sludge is replaced for fly ash at higher replacement content. The addition of alum sludge to the mix improved some properties such as density, strength, water absorption, and the elevated temperature behavior. It was observed that the addition of alum sludge was optimum at the 50% replacement level. The addition of alum sludge up to 50% significantly increased the compressive strength of mortar (up to 80% increase in 28 days strength). The compressive strength of the paste and mortar increased with an increase in curing age. Thus, alum sludge and fly ash can be employed together in the production of eco-friendly cementing material for environmental sustainability.