This paper investigated the antibacterial mechanism of spermidine-capped carbon dots (S-PCDs) against Staphylococcus aureus. The results showed that there were a large number of amino groups on the surface of S-PCDs and they had a high positive charge (+47.06 mV), which could be adsorbed on the negatively charged bacterial surface through electrostatic interaction and changed the permeability of the bacterial cell membrane. The extracellular protein and nucleic acid contents of S. aureus treated with S-PCDs were 5.4 and 1.2 times higher than those of the control group, respectively. The surface folds and defects of the bacterial cell membrane, and the leakage of cell contents were observed using SEM and TEM. The expression of metabolic oxidation regulatory genes dmpI, narJ and narK was upregulated and the intracellular ROS generation was induced, causing bacterial oxidative stress and eventually bacterial death. S-PCDs can effectively inhibit biofilm formation and had low cytotoxicity. The S-PCD treatment successfully inhibited microbial reproduction when pasteurized milk was stored at 25 °C and 4 °C. These results provide important insights into the antimicrobial mechanism of S-PCDs and lay the foundation for their application in the food field as a potentially novel bacteriostatic nanomaterial.

This study aimed to synthesize antibacterial carbon quantum dots (SP-CDs) from polyethyleneimine and spermidine via hydrothermal reaction. It was revealed that SP-CDs, with small size (7.18 nm) and high positive charge (+31.15 mV), had good fluorescence properties and lots of amino groups on their surfaces. The inhibition effect of SP-CDs on Staphylococcus aureus was better than that towards Escherichia coli, and the SP-CDs also had an inhibitory effect on multi-drug-resistant E. coli. The mechanism of SP-CDs shows that the SP-CDs were adsorbed on the surface of the negatively charged cell membrane through electrostatic interaction. SP-CDs can cause changes in membrane permeability, resulting in a shift of the cell membrane from order to disorder and the decomposition of chemical components, followed by the leakage of cell contents, resulting in bacterial death. SP-CDs can also significantly inhibit biofilm formation, destroy mature biofilms and reduce the number of living cells. Moreover, SP-CDs had negligible antimicrobial resistance even after 18 generations of treatment. This study proves that SP-CDs effectively inhibit the proliferation of foodborne pathogens, providing new feasibility for the application of carbon-based nanomaterials in the food industry.

The effects of NaCl (1–3%) and kansui (0.5–1.5%) on the quality of frozen cooked noodles (FCNs) were investigated, which provided a reference for alleviating the quality deterioration of FCNs. Textural testing illustrated that the optimal tensile properties were observed in 2% NaCl (N-2) and the maximum hardness and chewiness were reached at 1% kansui (K-1). Compared to NaCl, the water absorption and cooking loss of recooked FCNs increased significantly with increasing kansui levels (p < 0.05). Rheological results confirmed NaCl and kansui improved the resistance to deformation and recovery ability of thawed dough; K-1 especially had the highest dough strength. SEM showed N-2 induced a more elongated fibrous protein network that contributed to the extensibility, while excessive levels of kansui formed a deformed membrane-like gluten network that increased the solid loss. Moisture analysis revealed that N-2 reduced the free water content, while K-1 had the lowest freezable water content and highest binding capacity for deeply adsorbed water. The N-2 and K-1 induced more ordered protein secondary structures with stronger intermolecular disulfide bonds, which were maximally improved in K-1. This study provides more comprehensive theories for the strengthening effect of NaCl and kansui on FCNs quality.