This study introduces an innovative photolithography-based method for patterning ionic and inorganic particle materials such as silver iodide (AgI). Conventional methods lack precision when patterning powdered materials, which limits their applicability. The proposed method stacks layers of a particle material (AgI) and negative-tone photoresist for simultaneous ultraviolet exposure and development, resulting in well-defined AgI patterns. The sintering process successfully removed binders from the material layer and photoresist, yielding standalone AgI patterns on the Si substrate with good adhesion. The pitch remained consistent with the design values of the photomask when the pattern size was changed. In-situ observation of condensation frosting on the patterns was conducted, which confirmed the practicality of the developed patterning process. This versatile method is applicable to large areas with a high throughput and presents new opportunities for modifying functional surfaces.

A superheated steam fluidized bed dryer (SSFBD) in a self-heat recuperative configuration has a great potential of improving thermal efficiency of a lignite-fired power plant by recovering both of latent heat of vaporization of water kept in the fuel and part of sensible heat during the fuel processing. However, the optimal design of the dryer requires the fundamental knowledge of drying characteristics in respect to the individual properties of the utilized fuel. Experimental investigation to determine the correlation between a specific coal properties originated from geological background and its drying characteristics is thus the major concern in this paper. The investigated lignite is a representative of Turoszow deposit in Poland. Experimental attempts unveiling drying kinetics were carried out for 5 mm and 10 mm diameter spherical samples in the superheated steam atmosphere in the temperature range of 110 °C–170 °C. Simultaneous and continuous measurements of changes in weight, surface and interior temperatures and appearance on each tested sample were carried out for describing drying behavior. Analytical investigation was applied to explain the drying characteristics, which are strongly affected by the individual properties of coal and the inherent ash composition.

The influence of current collector on the sudden deterioration phenomena of conventional nickel-yttria-stabilized zirconia composite solid oxide fuel cell (SOFC) anodes operated in hydrogen with high humidity concentration is investigated. Current collectors of different materials have been tested within different conditions. It is found that the loss of contact between current collector mesh and the top surface of an anode cause the sudden deterioration of the anode. Platinum and gold current collector meshes have been proven to lead to the sudden deterioration of an anode in short time operation in high humidity conditions in conventional SOFC operation temperatures.