The influence of solid solution treatment (SST), artificial aging treatment (AAT), and deep cryogenic-aging treatment (DCAT) on the mechanical properties and microstructure evolution of 6082 aluminum alloy was investigated. The tensile test was performed to obtain the true stress–strain curves through an electronic universal testing machine. The results show that the yield strengths of the SST specimens in all three directions are the lowest, of less than 200 MPa. In addition, the maximum elongation of the SST specimen is over 16% and the value of in-plane anisotropy (IPA) is 5.40%. For the AAT specimen, the yield strengths of the AAT alloy in three directions have distinct improvements, which are beyond 340 MPa. However, the maximum elongation and the IPA were evidently reduced. The yield strength and elongation of the DCAT alloy exhibit a slight enhancement compared with those in the AAT condition, and the corresponding IPA is 0.61%. The studied alloy specimens in all conditions exhibit ductile fracture. The DCAT alloy has the highest density of precipitates with the smallest size. Therefore, the dislocation pinning effect of the DCAT specimens are the strongest, which exhibit the highest yield strength accordingly. In addition, the uniformly distributed precipitates in the matrix with a large ratio of long and short axes can suppress the anisotropy caused by elongated grains.

Hot compression tests were conducted to explore the deformation behavior of an extruded 7075 aluminum alloy bar at elevated temperatures. Specimens with 0°, 45°, and 90° angles along the extrusion direction were prepared. The compression temperatures were 300 and 400 °C, and the strain rates ranged from 0.001 to 0.1 s⁻¹. The corresponding microstructures were characterized via OM and TEM, and the macroscopic texture was tested using XRD. The results indicated that the strength of the 7075 alloy decreases with higher compression temperatures and is in a proportional relationship with respect to the strain rate. During high-temperature compression, it is easier to stimulate atomic diffusion in the matrix, which can improve thermal activation abilities and facilitate dynamic recovery and dynamic recrystallization. In addition, the coarsening of precipitates also contributed to dynamic softening. When compressed at 300 °C, the stress levels of the 0° specimens ranked first, and those for the 45° specimens were the lowest. When compressed at 400 °C, the flow stresses of the specimens along three directions were comparable. The anisotropic mechanical behavior can be explained by the fiber grains and brass {011} texture component. However, higher temperature deformation leads to recrystallization, which can weaken the anisotropy of mechanical properties.

The tensile properties of rolled 6082-T6 aluminum alloy were tested at a high temperature, and the influences of tensile temperature on its flow stress and anisotropy were studied. The microstructure evolution was characterized using optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). It was concluded that the tensile strength of the studied alloy decreases with increasing temperature. In higher-temperature deformation, the dislocation density decreases alongside the coarsening of precipitates, leading to a decrease in deformation resistance, and increase in the number of dimples and deepening of their sizes, exhibiting good plasticity. The alloy displays anisotropic mechanical properties at 200 °C due to the elongated grains and the orientation of the α-phase. The anisotropy becomes weaker with increasing temperature. There is no evident anisotropy at 400 °C, as the slip systems are activated more easily and the grains begin to recrystallize.

This study investigates the impact of cryogenic treatment duration on the mechanical properties and microstructural evolution of 6082 aluminum alloy subjected to subsequent artificial aging. Tensile tests were conducted using an electronic universal testing machine, and the microstructure was characterized by employing optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results indicate that both the tensile strength and elongation of the alloy first increase and then decrease with the extension of cryogenic treatment duration. The alloy treated with 12 h of cryogenic treatment followed by artificial aging at 180 °C for 8 h achieved a peak strength of 390 MPa. Meanwhile, the alloy treated with 8 h of cryogenic treatment and the same artificial aging process reached a maximum elongation of 13%. All specimens of 6082 aluminum alloy subjected to cryogenic and aging treatments exhibited ductile fracture under room temperature tensile conditions. The size of dimples at the fracture surface first increased and then decreased with increasing cryogenic treatment duration, indicating a transition from deeper to shallower dimples. The cryogenic treatment did not significantly affect the grain size of the alloy, which remained approximately 230 µm on average. Cryogenic treatment facilitated the precipitation of fine, densely distributed precipitates, enhancing the pinning effect of dislocations and thus improving the tensile strength. Additionally, cryogenic treatment increased the dislocation density and promoted the formation of subgrains, while the grain boundary precipitates transitioned from a continuous to a discontinuous distribution, all of which contribute to the enhancement of the plasticity.

The investigation of thermal deformation behavior plays a significant role in guaranteeing the overall performance of alloy materials. In this manuscript, a series of isothermal compression tests at different temperatures (300, 350, 400, and 450 °C) and strain rates (0.001, 0.01, 0.1, and 1 s⁻¹) were conducted to study the thermal deformation behavior of 7075 aluminum alloy. Subsequently, processing maps at a strain from 0.4 to 1.39 were established according to the stress–strain data obtained from various deformation parameters. The microstructural evolution of the target alloy was observed with an optical microscope and transmission electron microscope. The results reveal the unstable regions are located at (360–450 °C, 0.04–1 s⁻¹) and (300–315 °C, 0.01–0.22 s⁻¹). Precipitation particles, pinned dislocations, and highly dislocated areas can be observed in the microstructure of the alloy in the unstable regions. This is a potential crack and defect formation point. The identified optimum processing parameters are located at (375–450 °C, 0.001–0.03 s⁻¹), with a maximum dissipation efficiency of 0.6.

The hot compression of rolled 7075 alloys with different heat treatments was performed. The temperature ranged from 200 to 400 °C, and the strain rate was 0.01 s⁻¹. The stress level decreases with the increasing temperature during compression, and the strength of the alloy in the original condition is higher than that of solution-treated (ST) alloy at the same deformation condition. The alloys with different heat treatments exhibit different anisotropic behaviors at 200 °C; the anisotropy for the alloys in both conditions becomes weaker with increasing temperature. Then, the corresponding microstructure was studied. The alloy’s microstructure in its original condition consists of fiber grains; however, many equiaxed grains are found after solution treatment due to the recrystallization. The grains with different shapes lead to different anisotropic mechanical properties. For the alloys in both conditions, the density of the dislocation decreases with increasing temperature during compression, and a certain number of subgrains were found when deformed at 400 °C due to the higher driving force and a higher rate of atomic migration. Meanwhile, it is observed that the precipitates of the alloy become coarser during higher-temperature deformation. Dynamic softening is dominant in high-temperature deformation, decreasing stress during hot deformation.