In order to explore the hot deformation behaviors of the as-cast 7005 aluminum alloy, a number of hot tensile tests with four temperatures (100, 200, 300, and 400 °C) and three strain rates (0.001, 0.01, and 0.1 s⁻¹) were performed. The Johnson–Cook model was used to express the relationship between stress, strain, strain rate, and temperature. Scanning electron microscopy (SEM), optical microscopy (OM), and transmission electron microscopy (TEM) were selected to reveal fracture features and microstructure evolution of the studied alloy. The results indicate that the flow stress level of the alloy reduces with increases in the deformation temperature and decreases in the strain rate. The established Johnson–Cook model can be employed to characterize the thermal flow behavior of the experimental alloy. The grains near the fracture surface were elongated, and a certain number of holes were found after deformation at 400 °C. The alloy exhibits obvious ductile fracture features. The dimple is deep with high quantity. Due to the plastic deformation, a high-density dislocation structure is found in the material. High-temperature conditions promote the annihilation of dislocation, and, as a result, the dislocation density decreases gradually with the increase in temperature. In addition, a certain number of precipitates were found in the alloy after high-temperature tension.

The hot compression of rolled 7075 alloys with different heat treatments was performed. The temperature ranged from 200 to 400 °C, and the strain rate was 0.01 s⁻¹. The stress level decreases with the increasing temperature during compression, and the strength of the alloy in the original condition is higher than that of solution-treated (ST) alloy at the same deformation condition. The alloys with different heat treatments exhibit different anisotropic behaviors at 200 °C; the anisotropy for the alloys in both conditions becomes weaker with increasing temperature. Then, the corresponding microstructure was studied. The alloy’s microstructure in its original condition consists of fiber grains; however, many equiaxed grains are found after solution treatment due to the recrystallization. The grains with different shapes lead to different anisotropic mechanical properties. For the alloys in both conditions, the density of the dislocation decreases with increasing temperature during compression, and a certain number of subgrains were found when deformed at 400 °C due to the higher driving force and a higher rate of atomic migration. Meanwhile, it is observed that the precipitates of the alloy become coarser during higher-temperature deformation. Dynamic softening is dominant in high-temperature deformation, decreasing stress during hot deformation.

The hot tensile behavior of an extruded 6082 alloy sheet at varying temperatures and strain rates was investigated by a Gleeble3500 thermal simulation testing machine. The optical microscope (OM), scanning electron microscope (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD) were applied to observe the microstructure evolution. It is found that the flow stress of the studied alloy declines with increasing deformation temperature. When deformed at high temperatures, the density of dislocation decreases obviously. In addition, precipitate coarsening occurs, resulting in a decrease in deformation resistance. The dimple number of the fracture samples increases with temperature and the size of the dimple becomes deeper, exhibiting an excellent plasticity. The 6082 sheet presents anisotropy of mechanical behavior at 300 °C, this can be attributed to the fibrous grain and the Brass component {011}. The anisotropic behavior seems to be slighter with an increase in temperature. No obvious anisotropic behavior was found when tensiled at 400 °C. Because it is easier to activate the slip system at elevated temperatures, meanwhile, the recrystallization begins to occur at 400 °C.

High strain rate multiple forging (HSRMF) with pass strain ranging from 0.1 to 0.35 was carried out on the AZ31 magnesium alloy, and the microstructure, texture and mechanical properties were examined. The initial grain can be refined through the formation of high density {102} and {101(-)1}-{101(-)2} twins and subsequently twining induced dynamic recrystallization (DRX). The grain refinement of the HSRMFed alloy was affected by the lamellar thickness of the twin. Lower pass strain (Δε = 0.1) during HSRMF leads to the thick twin lamellae and consequently results in coarse DRX grain, meanwhile, an incomplete DRX occurs. While the twin lamellae thickness decreases with increasing pass strain, and a saturate thickness can be achieved with higher pass strain (Δε = 0.16–0.35), which results in the finer DRX structure. Homogeneous DXR structure can be obtained only at a proper accumulated strain (∑Δε = 0.96–1.4) during HSRMF, under lower accumulated strain, the DRX is insufficient, while higher accumulated strain leads to abnormal grain growth. A double peak basal texture was achieved at lower pass strain (Δε = 0.1), which developed into titled basal texture, and the texture intensity increases with the pass strain. HSRMFed alloys with homogeneous fine DRX grain and relatively weak texture show high strength and excellent ductility, therefore, and it is inferred that the optimum pass strain and accumulated strain range are 0.16–0.35 and 0.96–1.4 respectively.

The cold-rolled 2024 aluminum alloy sheets were subjected to solution treatments at different temperatures followed by artificial aging. The microstructure and mechanical properties were investigated using Vickers microhardness testing, tensile testing, optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that as the solution temperature increases, the coarse particles gradually dissolved into the matrix. At a solution temperature of 500 °C, the grains become nearly equiaxed with an average size of ~16.47 μm, and no significant grain growth is observed compared to the as-rolled condition. The refined microstructure contributes to excellent mechanical properties. In contrast, when the solution temperature increases to 550 °C, the microstructure shows severe grain coarsening (up to ~61.39 μm), which indicates that overburning occurs, resulting in a drastic deterioration in mechanical performance. As the aging time increases, precipitates become more uniformly and densely distributed throughout the matrix, and the hardness initially increases and reaches a peak after approximately 6 h of aging at 180 °C. The optimal mechanical performance, characterized by a favorable combination of strength and ductility, is achieved at an aging time of 6 h. In summary, the optimal heat treatment condition for the cold-rolled 2024 aluminum alloy sheet is solution treatment at 500 °C for 1 h followed by aging at 180 °C for 6 h, resulting in a hardness of 154 HV, a tensile strength of 465 MPa and an elongation of 13%.

The tension behaviors of Al-Mg alloys were tested, and the influences of deep cryogenic treatment (DCT) and grain size on their tensile properties were explored. Optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to characterize the evolution of the microstructure. It was concluded that the alloys with fine grain (FG) had a higher strain hardening capacity and strength, however, the alloys with coarse grain (CG) exhibited better plasticity. This can be explained by the alloy with fine grains having a higher density of grain boundary, which can hinder the motion of the dislocation; therefore, the deformation resistance was improved. For alloys with coarse grains, the dislocation has more freedom to move and is easier to rearrange, which is beneficial to the plasticity. Moreover, when given deep cryogenic treatment, the strength and plasticity of the alloys can be slightly improved, which can be attributed to the microplastic deformation that occurs during cryogenic treatment that can induce internal stress, as cold-induced internal stress is conductive in achieving a finer grain and higher density of dislocation.