The aim of this work was to investigate the structural features of type I collagen isoforms and collagen-based films at atomic and molecular scales, in order to evaluate whether and to what extent different protocols of slurry synthesis may change the protein structure and the final properties of the developed scaffolds. Wide Angle X-ray Scattering data on raw materials demonstrated the preferential orientation of collagen molecules in equine tendon-derived collagens, while randomly oriented molecules were found in bovine skin collagens, together with a lower crystalline degree, analyzed by the assessment of FWHM (Full Width at Half Maximum), and a certain degree of salt contamination. WAXS and FT-IR (Fourier Transform Infrared) analyses on bovine collagen-based films, showed that mechanical homogenization of slurry in acidic solution was the treatment ensuring a high content of super-organization of collagen into triple helices and a high crystalline domain into the material. In vitro tests on rat Schwannoma cells showed that Schwann cell differentiation into myelinating cells was dependent on the specific collagen film being used, and was found to be stimulated in case of homogenization-treated samples. Finally DHT/EDC crosslinking treatment was shown to affect mechanical stiffness of films depending on collagen source and processing conditions.

In recent years, the presence of numerous xenobiotic substances, such as antibiotics, has been detected in water environments. They can be considered as environmental contaminants, even if their effect on human health has yet to be totally understood. Several approaches have been studied for the removal of these kinds of pollutants. Among these compounds, tetracycline (TC), a broad-spectrum antibiotic, is one of the most commonly found in water due to its widespread use. In the context of reducing the presence of TC in aqueous solution, in this contribution, a composite catalyst based on zinc oxide (ZnO) and iron oxide (γ-Fe₂O₃) was developed and its photocatalytic properties were investigated. The catalytic materials were synthesized by a microwave-assisted aqueous solution method and characterized by Field Emission Scanning Electron Microscope (FESEM), X-Ray Fluorescence (XRF) and Brunauer−Emmett−Teller (BET) analysis. The TC concentration was evaluated by spectrophotometer measurements at specific time intervals. The performed photocatalytic experiments clearly demonstrated that the ZnO/γ-Fe₂O₃ composite catalyst presents significant photocatalytic activity, indeed a TC degradation efficiency of 88.52% was registered after 150 min. The presence of iron oxide in the structure of the catalyst enhances both the surface area and the pore volume, facilitating the adsorption of the analyte on the surface of nanostructures, a fundamental phase to optimize a photodegradation process. Moreover, ZnO was found to play the key role in the photocatalytic process assisted by γ-Fe₂O₃ which enhanced the TC degradation efficiency by 20%.