The one-pot process, which combines the polymerization of polyaniline (i.e., PANI) with subsequent reduction of iron nanowire (i.e., Fe NW) under a magnetic field, was developed to produce Fe@PANI core–shell nanowires. The synthesized nanowires with various PANI additions (0–30 wt.%) were characterized and used as microwave absorbers. Epoxy composites with 10 wt.% absorbers were prepared and examined using the coaxial method to reveal their microwave absorbing performance. Experimental results showed that the Fe NWs with PANI additions (0–30 wt.%) had average diameters ranging from 124.72 to 309.73 nm. As PANI addition increases, the α-Fe phase content and the grain size decrease, while the specific surface area increases. The nanowire-added composites exhibited superior microwave absorption performance with wide effective absorption bandwidths. Among them, Fe@PANI-90/10 exhibits the best overall microwave absorption performance. With a thickness of 2.3 mm, effective absorption bandwidth was the widest and reached 3.73 GHz, ranging from 9.73 to 13.46 GHz. Whereas with a thickness of 5.4 mm, Fe@PANI-90/10 reached the best reflection loss of −31.87 dB at 4.53 GHz.

Global energy sources are limited, and energy requirements are ever-increasing due to the demand for developments in human life and technology. The environmentally friendly direct formic acid fuel cell (DFAFC) is an attractive electronic device due to its clean energy. In a DFAFC, an anodic catalyst plays an important role concerning the oxidation pathway and activity. In the present study, palladium (Pd) was synthesized by synchrotron X-ray photoreduction using various irradiation times (0.5–4 min) to control the particle size. An acid-treated carbon nanotube (A-CNT) was used as the template for Pd deposition. The A-CNT and Pd/A-CNT were examined using scanning electron microscopy, X-ray diffraction, Raman spectroscopy, and transmission electron microscopy to reveal the microstructural characteristics. Electrochemical evaluation, electrocatalytic activity, and the DFAFC performance of so-obtained Pd/A-CNT catalysts were investigated. The experiment’s results showed that the Pd/A-CNT-2 (i.e., synchrotron photoreduction for 2 min) underwent a direct formic acid oxidation pathway and possessed a high ECSA value of 62.59 m²/g_Pd and superior electrocatalytic activity of 417.7 mA/mg_Pd. In a single DFAFC examination, the anodic Pd/A-CNT-2 catalyst had a power density of 106.2 mW/mg_Pd and a relatively long lifetime of 2.91 h. Pd/A-CNT-2 anodic catalysts synthesized by surfactant-free synchrotron X-ray photoreduction with a rapid processing time (2 min) are potential candidates for DFAFC applications.

Salisbury screen-type radar absorption structures (RASs) consisting of a resistance sheet, a spacer, and a conductive base provide an efficient method for microwave absorption. An impedance-matched resistance sheet allows microwaves to enter, whereas superior microwave absorbers enhance their performance further. In the present work, an impedance matching composite film was prepared by using polymer/iron/iron nanowires. By varying the polymer, poly (methyl methacrylate) (PMMA), poly (vinylidene fluoride) (PVDF), and poly (vinyl alcohol) (PVA), to iron powder ratios (1:1, 2:1, and 4:1), composite films were synthesized and examined by scanning electron microscopy, X-ray diffraction, and the four-point probe method to determine the materials’ characteristics. An impedance-matched composite film was prepared based on the selected composition with 1–10 wt.% iron nanowire additions. Experimental results showed that the polymeric composite film prepared by a ratio of iron-PVA of 4:1 exhibited a sheet resistance of 49 ± 9.7 Ω/sq due to well dispersion of iron powder in PVA. With 1 wt.% Fe nanowire addition, the optimal composite sheet resistance was 329.7 ± 45.3 Ω/sq, which corresponded to an impedance matching degree (i.e., |Z_in/Z₀| value) of 0.88 ± 0.12 and can be used as a resistance sheet for a Salisbury screen-type absorber in RAS applications.