In this work, we primarily aimed to study the Nb(V) doping effect on the surface activity and optical and electrical properties of nanocrystalline TiO₂ obtained through flame-spray pyrolysis. Materials were characterized using X-ray diffraction, Raman spectroscopy and IR, UV and visible spectroscopy. The mechanism of surface reaction with acetone was studied using in situ DRIFTs. It was found that the TiO₂-Nb-4 material demonstrated a higher conversion of acetone at a temperature of 300 °C than pure TiO₂, which was due to the presence of more active forms of chemisorbed oxygen, as well as higher Lewis acidity of the surface. Conduction activation energies (E_act) were calculated for thin films based on TiO₂-Nb materials. The results of the MB photobleaching experiment showed a non-monotonic change in the photocatalytic properties of materials with an increase in Nb(V) content, which was caused by a combination of factors, such as specific surface area, phase composition, concentration of charge carriers as well as their recombination due to lattice point defects.

Complex formation of α-, β-, and γ-cyclodextrins with sulfasalazine in biologically relevant buffer solutions (pH 1.2 and 7.4) was studied. Formation of inclusion complexes of 1 : 1 stoichiometry...