The purpose of this study was to optimize the processes of wetting fillers by varying the content of such additives as a surfactant and polymer in bitumen–mineral compositions in order to achieve optimal performance. The cosine of the contact angle was used as a criterion for assessing the adhesion of the bitumen binder to the surface of crushed stone. The effect of the additives’ concentration on surface tension and adhesive efficiency in binary and ternary bitumen compositions was studied. The following chemicals were used as additives: the original product AS-1, industrial additive AMDOR-10, and used sealant AG-4I, a product based on polyisobutylene and petroleum oils. AS-1 was obtained from the oil refining waste in the laboratory of M. Kozybayev North Kazakhstan University. The ternary “bitumen–AG-4I–AS-1” composition provided a maximum decrease in the contact angle by 15.96° (gray crushed stone) and by 14.06° (red crushed stone) relative to original bitumen, providing better wettability of the mineral filler particles with the bitumen, and as a result, maximum adhesion between the bitumen and crushed stone. The optimal performance of the bitumen–mineral composition was recorded with the joint presence of additives in the bitumen: AS-1 at a level of 1.0 g/dm3 and AG-4I at a level of 1.0 g/dm3.

The aim of the work was to study the effect of additive concentration on changes in the adhesive and cohesive strength of bitumen. To evaluate the effectiveness of modifiers in the composition of binary and triple bitumen systems in relation to mineral fillers of two grades, the method of determination of the adhesive efficiency and thermodynamic calculations of adhesion and cohesion work were used. The following compounds were used as additives: AS-2 synthesized from the oil refining waste and AG-4I (waste sealing liquid). Adhesion–cohesion processes in modified bitumen systems are limited by the wetting effect of crushed stone and the intensity of intermolecular forces in the condensed phase of the binder. In the binary compositions, the addition of modifiers into bitumen significantly improves the cohesive strength and adhesive efficiency in relation to crushed stone. The introduction of AS-2 into bitumen compositions with AG-4I increases adhesion efficiency and thermodynamic work of adhesion in relation to the filler surface. The adhesion efficiency and thermodynamic work of adhesion in the “bitumen-AG-4I-AS-2” system reach their maximum at C_AG-4I = 3.0 g/dm³ and C_AS-2 = 1.5 g/dm³. In these concentration modes, the composition ensures maximum increase in adhesion efficiency (A_KS = 65.18%; A_KA = 48.11%) and the greatest increase in thermodynamic work of adhesion (W_A(KS) = 15.79 mN/m; W_A(KA) = 14.13 mN/m).