This article presents the results of studying the disaggregation of titanium dioxide in water-dispersion compositions based on an acrylic film-forming agent under the action of a surfactant. The possibility of using polyether siloxane copolymer (PC) and sodium polyacrylate (NaPA) in paint and varnish compositions as modifying additives of the dispersing effect is proved. The correlation between the dispersing effect of surfactants and the amount of their adsorption on the pigment is proved. NaPA, which provides a greater reduction in adsorption strength, demonstrates a greater dispersing effect than PC. It was found that the larger the size of the aggregates of pigment particles, the greater the disjoining pressure created by the surfactant. An equation is derived that generalizes the cumulative contribution of surfactant concentration and the content of the film-forming agent in suspensions to the average particle diameter of pigment. The introduction of NaPA in the amount of 0.25 g/dm³ into the paint allows the rate of acid corrosion to be reduced by 2 times, the number of pores in the coating to be decreased, and the adhesion of the coating to be significantly increased (by 2 points according to ISO 11845: 2020).

This publication presents the results of studies of the bottom sediments (sapropels) of lakes in the North Kazakhstan region. The purpose of this study is to identify the possibility of using sapropels from the lakes of the region in obtaining innovative fertilizers for organic farming. For this purpose, geoinformation technologies, field research, statistics, and chemical and chemical-analytical methods were used (automated spectrometric methods of segmented flow analysis, photocolorimetry, flame photometry, and inductively coupled plasma atomic emission spectrometry). During the first stage of this study, the bottom sediments of three lakes in the region, which were at different stages of eutrophication, were selected to study the chemical composition of the raw materials. The sapropel of Lake Penkovskoye had optimal indicators. Further, an analysis of the territory of the region for the development of agrotourism was carried out. The aim of this study is to substantiate the prospects for the use of sapropel in the production of innovative fertilizers. The natural origin of sapropels allows them to be used in the production of environmentally friendly and safe products. Reducing the use of artificially synthesized mineral fertilizers will make agriculture and the environment safe and sustainable. This will further contribute to the development of agrotourism in the region.

The aim of this work is to optimize the composition of a two-component silicone enamel consisting of an aluminum pigment and a polyphenylsiloxane polymer to obtain the maximum dispersion of the pigment in the coating. The following products were used as surfactants: AS-1, PEPA, and Telaz. To assess the effect of surfactants on the dispersion of the pigment, computer-optical microscopy was used. The results of the studies showed that all the studied surfactants cause an improvement in the dispersion of the pigment. According to the degree of influence on the dispersion of the pigment, surfactants can be arranged in a row: PEPA > Telaz > AS-1. When the PEPA content in the enamel is 0.25 g/dm³, a decrease in the diameter of the pigment particles by 46% (from 26 to 14 microns) is recorded, with an increase in their specific amount by 2 times (from 258 to 550 pcs). Optimal enamel compositions allow a reduction in the corrosion rate by 11 times (from 0.6 to 0.053 mm/year) and improvement to the decorative properties of coatings (roughness, gloss, etc.). The effectiveness of the AS-1 product (obtained from oil refining waste) as a dispersant additive in silicone enamel has been proven.

The aim of this study was to optimize the composition of enamel consisting of aluminum pigment and polyphenylsiloxane polymer, in order to achieve the maximum aggregative stability of suspensions. Sedimentation rate (SR) was used as a criterion for assessing the aggregative stability of the suspensions. An original product, AS-1, and industrial additives PEPA and Telaz, were tested as surfactants. AS-1 was obtained from oil refining waste at M. Kozybayev North Kazakhstan University. All the studied surfactants improved the stability of the suspensions. The AS-1 additive significantly improved the stability of the suspensions, but exhibited a lower stabilizing ability by 10–20% than PEPA. The maximum overall stability of the suspensions was recorded at a PEPA level of 0.25–0.375 g/dm³ in the enamel. The Taguchi method was used to optimize the composition of the enamel, using AS-1 as the surfactant. It is recommended to use AS-1 in silicone enamels. Optimum compositions can reduce the petrol absorption of coatings by 1.5 times, their roughness by 2.5 times and increase their gloss.

The purpose of these studies was to establish the influence of the microstructural and rheological characteristics of modified bitumen compositions on the strength indicators of asphalt concrete. The effect of additives concentration on the rheological characteristics and microstructure of binary “bitumen–surfactant”, “bitumen-AG-4I”, and ternary “bitumen-AG-4I-AG-4I” systems has been studied. To assess the effect of bitumen dispersion on the physical and mechanical characteristics of modified asphalt concrete samples, the compressive strength value was determined. The following chemicals have been used as additives: the original product AS-1, industrial additive AMDOR-10, and used sealant AG-4I, a product based on polyisobutylene and petroleum oils. At an increased content of AG-4I (C ≥ 1.0 g/dm³) in ternary systems, the contribution of the emerging intermolecular polyisobutylene network to the development of structuring processes increases while the viscous effect of the surfactant AS-1 decreases. It has been established that the minimum size of bee-like bitumen structures (1.66 µm) is recorded with the joint presence of additives in the bitumen, AS-1 at a level of 1.0 g/dm³ and AG-4I at a level of 1.0 g/dm³. Under the same concentration regimes of the ternary bitumen composition, the maximum increase in compressive strength R_D was achieved with the smallest size of bee-like structures of modified bitumen.

Research has been conducted on the development of an innovative organomineral fertilizer based on local lake resources as a stimulator of germination and growth of crops, as one of the factors in achieving the goal of environmental sustainability. The results obtained are based on the environmental friendliness of the technology, increasing yields, and obtaining environmentally friendly products. This, in turn, will not only save mineral resources but also make it possible to use the resources from the bottom sediments of local lakes, and their rational extraction will contribute to the sustainable development and restoration of lake ecosystems. This article highlights the results of laboratory and field studies on the use of sapropel extract at the stage of pre-sowing seed treatment obtained by extraction of bottom sediments from lakes in Northern Kazakhstan. Solutions of aqueous alcohol extract of sapropel extract with concentrations of 0.4, 0.8, 1.2, 1.6, 2.0 g/L and table beet seeds (Beta vulgaris L.) of Bordo 237 variety were used as objects of research. Statistical analysis of laboratory experience data, based on the determination of germination energy and seed germination, allowed us to identify the optimal concentration of sapropel working solution for pre–sowing seed treatment—1.6 g/L. The index of germination energy and germination of seeds during pretreatment with sapropel extract of this concentration was 40% and 50%, respectively. This contributed to an increase in germination energy by almost 2 times and in seed germination by more than 40%. Pre-sowing treatment of seeds with sapropel extract at a concentration of 1.6 g/L in a field experiment contributed to the improvement of biometric indicators of beet fruits, such as diameter, length, and weight. The results of the data on fetal weight of the experimental variant compared with the control were 27% higher, and they were 26% and 32% higher compared with other experimental variants. In the experimental group, the highest yield index was also established, which is 2.15 times, or 53%, higher than the control, which emphasizes the effectiveness of pre-sowing seed treatment with the resulting sapropel suspension. A patent of the Republic of Kazakhstan was issued for the method we developed for obtaining a sapropel product for pre-sowing treatment of seeds: “A method for obtaining a sapropel product for pre-sowing treatment of vegetable seeds”. The research presented in the article confirms its effectiveness. The use of this product in pre-sowing seed treatment reduces the number of agrotechnological operations and costs, which makes this method more efficient and economically beneficial for the agricultural industry. Thus, the principle of food security will be implemented, contributing to the preservation of sustainable development and having a positive impact on the health of the population.