This article discusses the possibilities of using radiation cross-linked high density polyethylene (HDPEx) acting as a filler in the original high density polyethylene (HDPE) matrix. The newly created composite is one of the possible answers to questions relating to the processing of radiation cross-linked thermoplastics. Radiation cross-linked networking is—nowadays, a commonly used technology that can significantly modify the properties of many types of thermoplastics. This paper describes the influence of the concentration of filler, in the form of grit or powder obtained by the grinding/milling of products/industrial waste from radiation cross-linked high density polyethylene (rHDPEx) on the mechanical and processing properties and the composite structure. It was determined that, by varying the concentration of the filler, it is possible to influence the mechanical behaviour of the composite. The mechanical properties of the new composite—measured at room temperature, are generally comparable or better than the same properties of the original thermoplastic. This creates very good assumptions for the effective and economically acceptable, processing of high density polyethylene (rHDPEx) waste. Its processability however, is limited; it can be processed by injection moulding up to 60 wt %.

The development of ballistic materials has improved very rapidly in the last few years. Body armor plays an important role in protecting individuals during military threats. Body armor can be divided into hard and soft variants depending on the trade-offs between protection levels and wearer agility. Current research aims to optimize strength-to-weight ratios by using different combinations of synthetic or natural fibers or their combinations to achieve increasingly demanding requirements for ballistic materials. Moreover, it examines the various types of fibers utilized in the construction of body armor, ranging from traditional materials like metal and ceramic to synthetic and natural fibers. This paper discusses ongoing research efforts aimed at further enhancing the performance of these materials, such as the incorporation of modified natural fibers into advanced composite systems. The review provides a comprehensive analysis of the current state of the materials utilized in ballistic protection.

Some polymers need a cross-linking agent for the controlled cross-linking process of polymers with a tendency to degradation during the radiation cross-linking process. While, on the other hand, other polymers do not need a cross-linking agent—predominantly there are cross-linking polymers. The Thermo-Plastic Elastomer (TPE) that was used belongs to this group of predominantly cross-linking polymers; however, this agent is added because of faster reaction times and smaller irradiation doses. Microindentation–tensile and tensile impact tests were carried out on a thermoplastic sample—with, and without, a cross-linking agent. Small changes were measured between these materials at low radiation doses, (up to 66 kGy); nevertheless, at higher doses, the influence of the cross-linking agent on the mechanical properties is significant.

The goal of this research was to examine the effect of two surface modification methods, i.e., radiation cross-linking and plasma treatment, on the adhesive properties and the final quality of adhesive bonds of polypropylene (PP), which was chosen as the representative of the polyolefin group. Polymer cross-linking was induced by beta (accelerated electrons—β⁻) radiation in the following dosages: 33, 66, and 99 kGy. In order to determine the usability of β⁻ radiation for these applications (improving the adhesive properties and adhesiveness of surface layers), the obtained results were compared with values measured on surfaces treated by cold atmospheric-pressure plasma with outputs 2.4, 4, and 8 W. The effects of both methods were compared by several parameters, namely wetting contact angles, free surface energy, and overall strength of adhesive bonds. Furthermore, Fourier transform infrared (FTIR) spectroscopy and scanning electron microscopy (SEM) were conducted. According to our findings the following conclusion was reached; both tested surface modification methods significantly altered the properties of the specimen’s surface layer, which led to improved wetting, free surface energy, and bond adhesion. Following the β⁻ radiation, the free surface energy of PP rose by 80%, while the strength of the bond grew in some cases by 290% in comparison with the non-treated surface. These results show that when compared with cold plasma treatment the beta radiation appears to be an effective tool capable of improving the adhesive properties and adhesiveness of PP surface layers.

The main advantages of Thermoplastic Polyester Elastomers (TPE-E) are their elastomer properties as well as their ability to be processed in the same way as thermoplastic polymers (e.g., injection moulding, compression moulding and extrusion). However, TPE-Es’ properties, mainly their mechanical properties and thermal characteristics, are not as good as those of elastomers. Because of this TPE-Es are often modified with the aim of improving their properties and extending their range of application. Radiation cross-linking using accelerated electron beams is one of the most effective ways to change virgin polymers’ properties significantly. Their electrical (that is to say permittivity and resistivity measurements), mechanical (that is, tensile and impact tensile tests), as well as surface (that is, nano-indentation) properties were measured on modified/cross-linked TPE-E specimens with and/or without a cross-linking agent at irradiation doses of 0, 33, 66, 99, 132, 165 and 198 kGy. The data acquired from these procedures show significant changes in the measured properties. The results of this study allow the possibility of determining the proper processing parameters and irradiation doses for the production of TPE-E products which leads to the enlargement of their application in practice.

The temperature ageing of high-density polyethylene (HDPE) modified by accelerated electrons was studied. Commodity plastic HDPE was used as a basic polymer material which was modified by radiation cross-linking. This polymer was used because of its excellent processability and chemical resistance. Plastic injection molding technology was used for the production of test specimens. These specimens were modified with the dose of radiation 33, 66, 99, 132, 165, and 198 kGy. The prepared specimens were tested to determine: gel content, degree of swelling, temperature stability, and changes in mechanical properties after temperature ageing. The results were determined by scanning electron microscopy (SEM) analysis on the fracture surfaces. The results of this study confirm that modification of HDPE by radiation cross-linking has a significant effect on increasing temperature stability. It has been shown that HDPE modified by radiation cross-linking can withstand temperatures exceeding the melting point of the original HDPE for a short-term.