This study aimed to evaluate the fracture resistance of class II MOD cavities restored using different techniques and materials. Sixty extracted maxillary molars were selected and standardized class II MOD cavities were prepared using a custom-made paralleling device. The specimens were divided into four groups based on the restoration technique used: Group 1 (direct resin composite), Group 2 (short-fiber-reinforced composite resin), Group 3 (composite polyethylene fiber reinforcement), and Group 4 (CAD/CAM resin inlays). Fracture resistance was assessed for each group after thermocycling aging for 10,000 cycles. The mode of fracture was assigned to five types using Burke’s classification. To compare the fracture force among the tested materials, a paired sample t-test was performed. The significance level for each test was set at p < 0.05. Significant differences in fracture resistance were observed among the different restoration techniques. CAD/CAM inlays (2166 ± 615 N), short-fiber-reinforced composite resin (2471 ± 761 N), and composite polyethylene fiber reinforcement (1923 ± 492 N) showed superior fracture resistance compared to the group restored with direct resin composite (1242 ± 436 N). The conventional resin composite group exhibited the lowest mean fracture resistance. The choice of restoration material plays a critical role in the clinical survival of large MOD cavities. CAD/CAM inlays and fiber-reinforced composites offer improved fracture resistance, which is essential for long-term success in extensive restorations.

The aim of this research was to evaluate the abrasive dentin wear that can be induced by three commercial whitening toothpastes following a tooth-brushing simulation (TBS) corresponding to a three-month period. Sixty human canines were selected, and the roots were separated from the crowns. Then the roots were randomly divided into six groups (n = 10) and were submitted to TBS using the following slurries: Group 1—deionized water (RDA = 5); Group 2—ISO dentifrice slurry (RDA = 100); Group 3—a regular toothpaste (RDA = 70); Group 4—a charcoal-containing whitening toothpaste; Group 5—a whitening toothpaste containing blue covasorb and hydrated silica; and Group 6—a whitening toothpaste containing microsilica. Following TBS, surface loss and surface roughness changes were evaluated using confocal microscopy. Additionally, surface morphology and mineral content changes were observed using scanning electron microscopy and energy-dispersive X-ray spectroscopy. The deionized water group presented the lowest surface loss (p < 0.05), while the charcoal-containing toothpaste presented the highest surface loss, followed by ISO dentifrice slurry (p < 0.001). Blue-covasorb-containing and regular toothpastes did not present statistically significant differences (p = 0.245), and neither didmicrosilica-containing toothpaste or ISO dentifrice slurry (p = 0.112). The surface height parameters and surface morphology changes of the experimental groups followed the surface loss patterns, while no differences were detected in mineral content after TBS.Although the charcoal-containing toothpaste exhibited the highest abrasive wear to dentin, according to ISO 11609, all the tested toothpastes exhibited appropriate abrasive behavior towards dentin.

Immediate dentin sealing (IDS) is a method of improving the bond strength of indirect dental restorative materials to dentin and belongs to the biomimetic protocols of contemporary dentistry. The purpose of this systematic review was to evaluate the effect of IDS on the bond strength of resin-based CAD/CAM materials to dentin. PubMed and MEDLINE, Scopus, and the Web of Science were searched by two individual researchers, namely for studies that have been published in English between 1 January 2005 and 31 December 2023 in accordance with the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. The inclusion criteria encompassed articles related to in vitro studies, measuring the bond strength through microtensile bond strength (μ-TBS), micro-shear bond strength (μ-SBS), tensile bond strength (TBS) or shear bond strength (SBS) tests after the use of the IDS technique. The included restorative materials comprised resin-based CAD/CAM materials bonded to dentin. A total of 1821 studies were identified, of which 7 met the inclusion criteria. A meta-analysis was not deemed appropriate due to the high level of diversity inthe publications and techniques. The use of IDS yielded higher bond strength outcomesin various experimental conditions and resin-based CAD/CAM materials. Overall, IDS in CAD/CAM restorations may contribute to better clinical outcomesand improved restoration longevity due to this property.

(1) Background: In recent years, there has been a growing interest in understanding the innate immunity of the mouth, particularly the mechanisms through which vitamin D influences oral health. Researchers have increasingly focused on the association between vitamin D and the antimicrobial peptide LL-37 since the CAMP gene, responsible for encoding the LL-37 peptide, is a direct target of both vitamin D and its receptor (vitamin D receptor, VDR). This study aimed to explore the correlation between the 25-hydroxyvitamin D (25(OH)D) levels and the concentration of the LL-37 peptide in both serum and saliva. The objective was to compare the serum concentrations of 25(OH)D and ll-37 with those in saliva and to access the correlations between the two compounds. (2) Methods: Serum and whole saliva samples were collected from 72 healthy adults (mean age 28.68 ± 8.35). The levels of 25(OH)D and LL-37 were assessed in both the saliva and serum samples using commercially available enzyme-linked immunosorbent assay (ELISA) kits. (3) Results: The 25(OH)D levels in the serum (median 5.92 ng/mL, min–max 2.7–10.4 ng/mL) correlated with the LL-37 serum levels (62 ng/mL, min–max 18–378 ng/mL; Pearson’s r 0.328, p = 0.005). Additionally, the 25(OH)D levels in saliva (median 1.16 ng/mL, min–max 0.54–2.12 ng/mL) strongly correlated with the LL-37 salivary levels (median 44 ng/mL, min–max 6.5–205 ng/mL; Pearson’s r 0.667, p < 0.001). The 25(OH)D salivary levels demonstrated a robust correlation with the LL-37 salivary levels. (4) Conclusions: This discovery emphasizes the complex interplay between vitamin D and LL-37 and lay the groundwork for the further exploration of vitamin D’s role in oral immune function.

The aim of this laboratory study was to investigate and compare the impact of five desensitizing techniques as a treatment fortooth sensitivity on the exposed dentin after an in-office tooth bleaching procedure. Thirty intact human molars were collected for this investigation. The specimens were obtained by transversely cutting 2.5 mm of the crowns, leading to exposure of the dentin. The specimens were cleaned in an ultrasonic bath and treated initially with EDTA gel 15% for 4 min and then with Opalescence Boost bleaching gel (40% H₂O₂) for two sets of 20 min. Then, the samples were randomly divided into six groups (n = 5) and received one of the following treatments: Group 1 (no treatment—control group), Group 2 (Emofluor gel—0.4% SnF₂), Group 3 (MI Paste—CPP-ACPF), Group 4 (BioMinF paste—calcium phospho-fluoro-silicate), Group 5 (air-abrasion with ProSylc—Bioglass 45S5), and Group 6 (Er,Cr:YSGG laser). Subsequently, each sample was observed utilizing scanning electron microscopy (SEM) in order to detect the rate of occlusion of dentin tubules. SEM-EDS analysis revealed no occlusion of the dentin tubules in the control group, while Groups 2, 4, and 5 presented high effectiveness (>95% percentage of occluded tubules), and Groups 3 and 6 presented lower values (21.6 and 26.8%, respectively). It was concluded that althoughall the tested groups presented higher percentages of occlusion of the dentinal tubules compared to the control group, there were differences in effectiveness among them. The most effective treatments were the daily use of BioMinF paste and SnF₂-containing gel, as well as air-abrasion with ProSylc powder.