As a result of industrialization and environmental pollution, increasing importance is being given to eco-friendly materials and technology. In particular, eco-friendly biocomposites using polylactic acid (PLA) have attracted great interest. In this work, fiber-reinforced composites were investigated in order to enhance the mechanical properties and improve the economic efficiency of PLA. Specifically, composite materials using natural fibers, such as kenaf were actively studied. In the utilization of natural fibers, such as kenaf, the treatment method for increasing the bonding force between the fiber and the matrix is very important. In this study, the surface of kenaf was treated using an acetylation technique, and the PLA composite material was prepared using surface-treated kenaf. Changes in fiber properties were observed with acetylation treatment time. The mechanical properties, thermal stability, and water absorption resistance of the acetylated kenaf and PLA composites prepared for each condition were evaluated. Finally, was concluded that acetylation treatment is effective for improving the performance of PLA/kenaf composites. This behavior was found to relate to the surface cleaning of acetylated kanaf, in addition to the efficient modification of the hydrophilic characteristics of kenaf.

This article reports effect of vibration duration of high ultrasound applied to bio-composite while gelatinized on its properties. The bio-composite consists of mixing of both the tapioca starch based bioplastic and oil palm empty fruit bunch (OPEFB) fibers with high volume fraction. Gelatinization of the bio-composite sample was poured into a rectangular glass mold placed then in an ultrasonic bath with 40kHz, and 250watt in different duration for 0, 15, 30, 60min respectively. The results show that vibration during gelatinization has changed the characterisation of the bio-composite. SEM photograph displayed different fracture surface of tensile sample. For vibration duration of 60min, tensile strength (TM), and tensile modulus (TM) was improved to 64.4, 277.4%, respectively, meanwhile strain was decreased to 35.1% in comparison without vibration. Fourier Transform Infrared Spectroscopy (FTIR), and XRD diffraction of the bio-composite has changed due to various vibration duration. Moisture absorption of the vibrated bio-composite was lower than that of the untreated one.