The current work investigates the viability of utilizing a friction stir deposition (FSD) technique to fabricate continuous multilayer high-performance, metal-based nanoceramic composites. For this purpose, AA2011/nano Al₂O₃ composites were successfully produced using AA2011 as a matrix in two temper conditions (i.e., AA2011-T6 and AA2011-O). The deposition of matrices without nano Al₂O₃ addition was also friction stir deposited for comparison purposes. The deposition process parameters were an 800 rpm rod rotation speed and a 5 mm/min feed rate. Relative density and mechanical properties (i.e., hardness, compressive strength, and wear resistance) were evaluated on the base materials, deposited matrices, and produced composites. The microstructural features of the base materials and the friction stir deposited materials were investigated using an optical microscope (OM) and a scanning electron microscope (SEM) equipped with an EDS analysis system. The worn surface was also examined using SEM. The suggested technique with the applied parameters succeeded in producing defect-free deposited continuous multilayer AA2011-T6/nano Al₂O₃ and AA2011-O/nano Al₂O₃ composites, revealing well-bonded layers, grain refined microstructures, and homogeneously distributed Al₂O₃ particles. The deposited composites showed higher hardness, compressive strengths, and wear resistance than the deposited AA2011 matrices at the two temper conditions. Using the AA2011-T6 temper condition as a matrix, the produced composite showed the highest wear resistance among all the deposited and base materials.

Selecting an economically suitable welding technique and optimizing welding parameters to obtain high joint quality is considered a challenge for expanding the 5xxx aluminum alloy series in various industrial applications. This work aims to investigate the effect of applying different welding techniques, tungsten inert gas (TIG) and metal inert gas (MIG), as fusion welding processes compared to friction stir welding (FSW), a solid-state joining process, on the joint performance of the produced 5 mm thick similar AA5083-H111 butt weldments at different welding conditions. Different methods were used to evaluate the quality of the produced joints, including visual inspection, radiographic testing (RT), and macrostructure evaluation, in addition to hardness and tensile tests. The fracture surface of the tensile-failed specimens was also investigated using a scanning electron microscope (SEM). Furthermore, the current study ended with an economic analysis of the welding techniques used. The results showed that, for the friction stir-welded joints, the radiographic films revealed defect-free joints at the two applied travel speeds of 100 mm/min and 400 mm/min and a constant tool rotating speed of 400 rpm. In addition, only one joint was welded by MIG at a welding current of 130 Amp, with a 19 L/min flow rate of pure argon. In contrast, the radiographic films showed internal defects such as lack of fusion (LOF), lack of penetration (LOP), and porosity (P) for the two joints welded by TIG and one joint welded by MIG. The hardness of the welded joints was enhanced over the AA5083-H111 base material (BM) by 24–29, 31–35, and 46–50% for the MIG, TIG, and FSW joints, respectively. The maximum ultimate tensile strength was obtained for the FSW joint welded at a 400 mm/min travel speed. Adopting FSW in shipbuilding applications can further produce the AA5083-H11 joints with higher quality and efficiency than fusion welding techniques such as MIG and TIG processes. In addition, time and cost comparisons between TIG, MIG, and FSW were performed for five-millimeter-thick and one-meter-long AA5083-H111.

In this work, three mathematical models for the heat generation during bobbin tool friction stir welding (BT-FSW) of aluminum using three tool pin geometries have been proposed. The models have utilized and updated the available models for the heat generation during the conventional tool friction stir welding (CT-FSW). For the validation of the models, BT-FSW experiments have been carried out for aluminum alloy AA1050 using three different pin geometries (cylindrical, square, and triangular), at different welding speeds of 200, 400, 600, 800, and 1000 mm/min and a constant tool rotation speed of 600 rpm. The welding temperatures during BT-FSW have been measured to be compared with that calculated from the models at the same parameters. It has been found that the calculated welding temperatures from the models and that measured during BT-FSW are in good agreement at all the investigated welding speeds especially in case of the square and cylindrical pins, proving the validity of the developed models for the predication of the heat generation as well as the welding temperatures. This will allow proper designing of the BT-FSW parameters and avoiding the conditions that can deteriorate the joint quality and properties.

Bobbin tool friction stir welding (BT-FSW) is characterized by a fully penetrated pin and double-sided shoulder that promote symmetrical solid-state joints. However, control of the processing parameters to obtain defect-free thick lap joints is still difficult and needs more effort. In this study, the BT-FSW process was used to produce 10 mm AA1050-H14 similar lap joints. A newly designed bobbin tool (BT) with three different pin geometries (cylindrical, square, and triangular) and concave shoulders profile was designed, manufactured, and applied to produce the Al alloy lap joints. The experiments were carried out at a constant tool rotation speed of 600 rpm and a wide range of various welding travel speeds of 200, 400, 600, 800, and 1000 mm/min. The generated temperature during the BT-FSW process was recorded and analyzed at the joints’ center line, and at both advancing and retreating sides. Visual inspection, macrostructures, hardness, and tensile properties were investigated. The fracture surfaces after tensile testing were also examined. The results showed that the pin geometry and travel speed are considered the most important controlling parameters in BT-FSW thick lap joints. The square (Sq) pin geometry gives the highest BT-FSW stir zone temperature compared to the other two pins, cylindrical (Cy) and triangular (Tr), whereas the Tr pin gives the lowest stir zone temperature at all applied travel speeds from 200 to 1000 mm/min. Furthermore, the temperature along the lap joints decreased with increasing the welding speed, and the maximum temperature of 380 °C was obtained at the lowest travel speed of 200 mm/min with applying Sq pin geometry. The temperature at the advancing side (AS) was higher than that at the retreating side (RS) by around 20 °C. Defect-free welds were produced using a bobbin tool with Cy and Sq pin geometries at all the travel welding speeds investigated. BT-FSW at a travel speed of 200 mm/min leads to the highest tensile shear properties, in the case of using the Sq pin. The hardness profiles showed a significant effect for both the tool pin geometry and the welding speed, whereas the width of the softened region is reduced dramatically with increasing the welding speed and using the triangular pin.

This study investigated the effect of a hemispherical friction stir welding (FSW) tool on the heat generation and mechanical properties of dissimilar butt welded AA5083 and AA7075 alloys. FSW was performed on the dissimilar aluminum alloys AA5083-H111 and AA7075-T6 using welding speeds of 25, 50, and 75 mm/min. The tool rotation rate was kept constant at 500 rpm. An analytical model was developed to calculate heat generation and temperature distribution during the FSW process utilizing a hemispherical tool. The experimental results were compared to the calculated data. The latter confirms the accuracy of the analytical model, demonstrating a high degree of agreement. Sound FSW dissimilar joints were achieved at welding speeds of 50 and 25 mm/min. Meanwhile, joints created at a welding speed of 75 mm/min exhibited a tunnel-like defect, which can be attributed to the minimal heat generated at this particular welding speed. At a lower welding speed of 25 mm/min, a higher tensile strength of the dissimilar FSWed joints AA5083 and AA7075 was achieved with a joint efficiency of over 97%.

The effect of nitrogen addition, heat input, and filler metals on weld metal microstructure and mechanical properties of alloy 316 ASS are studied. Autogenous gas tungsten arc welding (GTAW) is employed by adding up to 2vol. % N2 in Ar. These variables affect a number of welding aspects, including arc characteristics and microstructure. The influence of shielding gas mixtures on microstructure and mechanical properties of GTAW of austenitic 316 stainless steel is studied. Mechanical properties of welds are determined through uniaxial tension, hardness measurements, impact, and bending tests. Weld defects, as porosity and inclusions are examined using radiographic testing. Weld specimens are free of porosity, inclusions, and hydrogen cracking. Mechanical properties and cooling rate are lower at higher heat input, but the cooling time, nugget area, and solidification time are higher. The addition of N2 to Ar shielding gas leads to higher values of the ultimate tensile strength ‘UTS’, yield stress ‘YS’, and elongation percent. UTS, YS, and elongation of welds depend on heat input, filler metal, and N2 content of shielding gas. Finally, a mathematical model is built depending upon the welding current, filler metals, and shielding gases.