This study evaluated the effect of self-etching ceramic primer (SECP) on shear bond strength (SBS) of zirconia-reinforced lithium silicate (ZLS) ceramics. Two hundred and seventy block-specimens of two types of ZLS ceramics and one type of lithium disilicate (LS) ceramics were prepared. Ninety blocks of each material were divided into three groups (n = 30), namely group 1: no surface treatment (control), group 2: hydrofluoric acid (HF), silane-based primer (S), and group 3: SECP. Resin cement was applied, and light-cured for build-up. Shear bond strength (SBS) test was used. Half of the bonded specimens (n = 15) were tested after storage in distilled water for 24 h, whereas the other half were tested after 5000 thermo-cycles. The failure modes were evaluated using scanning electron microscope (SEM). The SBS values for samples treated with SECP and HF + S within the respective materials were statistically comparable (p > 0.05). Thermocycling significantly reduced the SBS (p < 0.05) for all ceramic materials in groups 2 and 3. Mixed failure followed by adhesive failure were the most common failure modes in groups 2 and 3, whereas pretest failure was only detected in group 1. Considering the limitations of the study, with respect to in vitro bond strength, the SECP is an alternative for the conditioning of internal surface of glass ceramics.

Tooth root caries account for 10.1% of all dental caries in the USA. This study developed a multifunctional resin coating with calcium (Ca) and phosphate (P) ion release and antibacterial properties to combat root caries. The effects of nano-sized amorphous calcium phosphate (NACP) and dimethylaminohexadecyl methacrylate (DMAHDM) on mechanical, physical, and antibacterial properties against Streptococcus mutans, and cytotoxicity on dental pulp stem cells and gingival fibroblasts were evaluated. A coating resin combining urethane dimethacrylate (UDMA), triethylene glycol divinylbenzyl ether (TEGDVBE), DMAHDM, and NACP was synthesized and compared with Seal&Protect and Vanish XT. Experimental groups (UV + 5% DMAHDM + 10%, 15%, and 20% NACP) showed flexural strength (70.9 ± 8.0 to 81.1 ± 6.0) MPa, significantly higher than Seal&Protect (48.2 ± 7.2) MPa (p < 0.05) and comparable to Vanish XT (70.2 ± 13.6) MPa, (p > 0.05). Elastic modulus (2.2 to 3.3) GPa was lower than Vanish XT (9.4 ± 1.1) GPa (p < 0.05). Experimental groups showed an 8 log CFU reduction, 96% reduction in metabolic activity and 87% in lactic acid production, and increased Ca (1.25 ± 0.03) mmol/L and P (0.8 ± 0.001) mmol/L release over 35 days. Cytotoxicity for experimental groups against dental pulp stem cells and human gingival fibroblast was low and matched those of commercial controls already used in clinic. The resin demonstrated potent antibacterial properties, high ion release, low cytotoxicity, and maintained physical and mechanical integrity, offering potential to prevent root caries formation and progression.

Objective: To evaluate the effects of surface treatment and repair material on the repair shear bond strength (SBS) of the bioactive restorative material. Methods: A total of 240 Activa BioActive Restorative (Activa) discs were prepared, aged, and polished, and divided randomly into eight groups ( n = 30). Groups 1–4 discs were repaired with bulk-fill flowable resin-based composite (Bulk-RBC), and Groups 5–8 discs with Activa. Surface treatment used for each repair material type were air abrasion with silica-coated 30-m Al₂O₃ particles (air abrasion) (Groups 2 & 6), Air abrasion with universal primer (Groups 3 & 7), and Air abrasion with universal adhesive (Groups 4 & 8). Groups 1 and 5 were controls without surface treatment. SBS test was performed, and the failure mode and surface topography were assessed. Results: Surface treatment with air abrasion significantly improved the SBS for repair using both Activa and Bulk-RBC. Repair SBS using Activa was significantly higher compared with Bulk-RBC. Cohesive failure in substrate and mixed failures were most common in the surface-treated groups (2–4, 6–8). Air abrasion produced prominent surface topography changes compared with polishing. Conclusion: Air abrasion enhances the repair SBS of aged bioactive restorative material. The use of the same material (Activa) for repair affords a higher bond strength compared with the use bulk-RBC.

Provisional crowns are often used in dentistry for prolonged periods, but bacterial attachment and dental plaque often lead to gingival inflammation and secondary caries. The aims of this research were to develop a novel resin-based antibacterial provisional crown coating to prevent secondary caries and investigate the physical properties and antibacterial efficacy. The resin-based coating was prepared by addition of triethylene glycoldivinylbenzyl ether and urethane dimethacrylate, with the antibacterial monomer dimethylaminododecyl methacrylate (DMADDM) incorporated at different mass fractions. Surface characteristics including surface roughness and contact angle were assessed. The antibacterial effects were evaluated by 48 h biofilms of Streptococcus mutans (S. mutans) on provisional crowns coated with the resin-based coating. No statistically significant difference was observed in surface roughness across all groups (p > 0.05), showing that adding DMADDM did not have a negative impact on surface roughness. The contact angle results revealed a significant difference in hydrophilicity between different concentrations of DMADDM (p < 0.01), but overall hydrophilicity did not negatively affect the performance of the coating. The incorporation of 5% DMADDM demonstrated a significant antibiofilm effect on S. mutans biofilm CFU with a 4-log reduction compared to controls (p < 0.01). Significant reductions of 4–5 folds were observed in biofilm metabolic activity and lactic acid production (p < 0.01). The findings suggest that the novel coating material could enhance the long-term performance and clinical outcomes of provisional crowns, contributing to better patient oral health.

Traditional pulp-capping materials like mineral trioxide aggregate (MTA) offer excellent biocompatibility and sealing, but limitations such as prolonged setting time, low bioactivity, and high costs persist. Metformin, with its potential in craniofacial regeneration, could enhance dentin synthesis by targeting pulp cells. This study aimed to: (1) develop a calcium phosphate cement with chitosan (CPCC) with improved physio-mechanical properties; (2) incorporate metformin (CPCC-Met) to assess release; and (3) evaluate human dental pulp stem cells (hDPSCs) response. CPCC was mixed at different powder-to-liquid ratios to evaluate physio-mechanical properties compared to MTA. The optimized CPCC formulation was loaded with 0, 50, 100, and 150 µg of metformin to measure release and assess hDPSCs attachment and proliferation (1, 4, and 7 d) via live/dead imaging and SEM. One-way ANOVA was used for statistical analysis. Results showed CPCC at a 3.25:1 ratio significantly reduced setting time to 41.5 min versus 123 min for MTA (p < 0.05). Metformin release correlated with concentration, and SEM confirmed the presence of a porous, hydroxyapatite-rich surface. Cell viability was consistently high across groups (>93% at 1 d, >95% at 4 d, ≈98% at 7 d), with no significant differences (p > 0.05). These findings suggest that the novel CPCC-Met demonstrates promise as a fast-setting, cost-effective pulp-capping material, offering metformin delivery to enhance dentin repair.