Cellulose aerogels have great prospects for noise reduction applications due to their sustainable value and superior 3D interconnected porous structures. The drying principle is a crucial factor in the preparation process for developing high-performance aerogels, particularly with respect to achieving high acoustic absorption properties. In this study, multifunctional cellulose nanocrystal (CNC) aerogels were conveniently prepared using two distinct freeze-drying principles: refrigerator conventional freezing (RCF) and liquid nitrogen unidirectional freezing (LnUF). The results indicate that the rapid RCF process resulted in a denser CNC aerogel structure with disordered larger pores, causing a stronger compressive performance (Young’s modulus of 40 kPa). On the contrary, the LnUF process constructed ordered structures of CNC aerogels with a lower bulk density (0.03 g/cm³) and smaller apertures, resulting in better thermal stability, higher diffuse reflection across visible light, and especially increased acoustic absorption performance at low–mid frequencies (600–3000 Hz). Moreover, the dissipation mechanism of sound energy in the fabricated CNC aerogels is predicted by a designed porous media model. This work not only paves the way for optimizing the performance of aerogels through structure control, but also provides a new perspective for developing sustainable and efficient acoustic absorptive materials for a wide range of applications.

Chlorophenylacetonitriles are known as one of the emerging nitrogenous disinfection byproducts (N-DBPs) in chlorinated drinking water due to their concerned cytotoxicity and genotoxicity compared to regulated carbonaceous DBPs. However, under low-dose exposure, the in vivo pathological consequences of chlorophenylacetonitriles remain largely unresolved. Here, C57BL/6J mice were exposed to 2-chlorophenylacetonitrile (2-CPAN) via drinking water (100 ug/L) for six months, and an integrated histopathological and genome-wide transcriptomic approach was employed to mechanistically characterize its multi-organ toxicological consequences. 2-CPAN ingestion significantly suppressed body weight (35.9 ± 2.0 g vs. 47.6 ± 11.6 g, p < 0.05) and induced severe gastroenteropathy—including gastric lamina propria inflammatory infiltration, intestinal villous blunting, crypt disorganization, transmural mononuclear infiltration, and abrogating epithelial barrier integrity. Intestinal barrier failure drove portal translocation of luminal PAMPs, potentially triggering splenic white pulp atrophy, red/white pulp boundary dissolution, and parenchymal changes consistent with fibrotic remodeling. Splenic RNA sequencing revealed a bipartite transcriptomic reprogramming: upregulated pathways were enriched in the ribosome, MAPK signaling, cytokine–cytokine receptor interaction, and chemokine signaling pathways. A proteotoxic stress module (Hspa1a, 9.4-fold; Hspa1b, 10.2-fold) and a chemokine effector hub (Ccl2, 3.43-fold; Ccl5, 2.9-fold; Ccl19, 2.58-fold; Ccl21a, 2.15-fold) were identified by the STRING network. Downregulated pathways converged on cell cycle suppression, with concurrent loss of Ccne1/Ccne2 and Cdc6 (G1/S block), Ccnb1 and Plk1 (G2/M arrest), and Rrm2/Tars3/TrnM (dNTP and aminoacyl-tRNA starvation), collectively forcing splenic lymphocytes into irreversible proliferative failure. These findings provide the first mechanistically resolved in vivo evidence that chronic 2-CPAN exposure drives a potential gut–spleen toxicological axis, underscoring the urgent need to incorporate organ endpoints by long-term exposure into N-DBP risk assessment.

Alite calcium sulfoaluminate (ACSA) cement is an innovative and environmentally friendly cement compared to ordinary Portland cement (OPC). The synthesis and hydration of ACSA clinkers doped with gradient sulfur were investigated. The clinker compositions and hydrated pastes were characterized by X-ray diffraction (XRD), isothermal calorimetry, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM) to analyze its mineral contents, hydration products, heat release, pore structure, and microstructure. The compressive strength and linear expansion of ACSA mortars were tested for their mechanical properties. Results showed that clinkers doped with 2 wt.% MgO can offset the hurdle that SO₃ caused to the formation of C₃S (tricalcium silicate). Clinkers with varying ratios of C₃S and C₄A₃$ (calcium sulfoaluminate) were obtained, achieving 58–70% C₃S and 2.0–5.6% C₄A₃$ in ACSA through adjusting the KH (lime saturation factor) values and SO₃ dosage. ACSA cement showed better early mechanical properties. The 0.93 KH value with 3% SO₃ dosage in the raw meal, which contains 63.9% C₃S and 2.98% C₄A₃$ in the clinker, reached an optimal compressive strength level at 1d (26.35 MPa) and at 3d (39.41 MPa), marking 30.45% and 18.70% increases compared to PII 52.5. The excellent early strength of ACSA cement may offer promising applications t increasing the incorporation of supplementary cementitious materials, thereby reduce pollution and carbon emissions.