The growth of InGaAs quantum wells (QWs) epitaxially on InP substrates is of great interest due to their wide application in optoelectronic devices. However, conventional molecular beam epitaxy requires substrate temperatures between 400 and 500 °C, which can lead to disorder scattering, dopant diffusion, and interface roughening, adversely affecting device performance. Lower growth temperatures enable the fabrication of high-speed optoelectronic devices by increasing arsenic antisite defects and reducing carrier lifetimes. This work investigates the low-temperature epitaxial growth of InAs/GaAs short-period superlattices as an ordered replacement for InGaAs quantum wells, using migration-enhanced epitaxy (MEE) with low growth temperatures down to 200–250 °C. The InAs/GaAs multi-quantum wells with InAlAs barriers using MEE grown at 230 °C show good single crystals with sharp interfaces, without mismatch dislocations found. The Raman results reveal that the MEE mode enables the growth of (InAs)₄(GaAs)₃/InAlAs QWs with excellent periodicity, effectively reducing alloy scattering. The room temperature (RT) photoluminescence (PL) measurement shows the strong PL responses with narrow peaks, revealing the good quality of the MEE-grown QWs. The RT electron mobility of the sample grown in low-temperature MEE mode is as high as 2100 cm²/V∗s. In addition, the photoexcited band-edge carrier lifetime was about 3.3 ps at RT. The high-quality superlattices obtained confirm MEE’s effectiveness for enabling advanced III-V device structures at reduced temperatures. This promises improved performance for applications in areas such as high-speed transistors, terahertz imaging, and optical communications.

The low-temperature-grown InGaAs (LT-InGaAs) photoconductive antenna has received great attention for the development of highly compact and integrated cheap THz sources. However, the performance of the LT-InGaAs photoconductive antenna is limited by its low resistivity and mobility. The generated radiated power is much weaker compared to the low-temperature-grown GaAs-based photoconductive antennas. This is mainly caused by the low abundance of excess As in LT-InGaAs with the conventional growth mode, which inevitably gives rise to the formation of As precipitate and alloy scattering after annealing. In this paper, the migration-enhanced molecular beam epitaxy technique is developed to grow high-quality (InAs)_m/(GaAs)_n short-period superlattices with a sharp interface instead of InGaAs on InP substrate. The improved electron mobility and resistivity at room temperature (RT) are found to be 843 cm²/(V·s) and 1648 ohm/sq, respectively, for the (InAs)_m/(GaAs)_n short-period superlattice. The band-edge photo-excited carrier lifetime is determined to be ~1.2 ps at RT. The calculated photocurrent intensity, obtained by solving the Maxwell wave equation and the coupled drift–diffusion/Poisson equation using the finite element method, is in good agreement with previously reported results. This work may provide a new approach for the material growth towards high-performance THz photoconductive antennas with high radiation power.

This investigation explores the structural and electronic properties of low-temperature-grown (InAs)₄(GaAs)₃/Be-doped InAlAs and InGaAs/Be-doped InAlAs multiple quantum wells (MQWs), utilizing migration-enhanced epitaxy (MEE) and conventional molecular beam epitaxy (MBE) growth mode. Through comprehensive characterization methods including transmission electron microscopy (TEM), Raman spectroscopy, atomic force microscopy (AFM), pump–probe transient reflectivity, and Hall effect measurements, the study reveals significant distinctions between the two types of MQWs. The (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs grown via the MEE mode exhibit enhanced periodicity and interface quality over the InGaAs/Be-InAlAs MQWs grown through the conventional molecule beam epitaxy (MBE) mode, as evidenced by TEM. The AFM results indicate lower surface roughness for the (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs by using the MEE mode. Raman spectroscopy reveals weaker disorder-activated modes in the (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs by using the MEE mode. This originates from utilizing the (InAs)₄(GaAs)₃ short period superlattices rather than InGaAs, which suppresses the arbitrary distribution of Ga and In atoms during the InGaAs growth. Furthermore, pump–probe transient reflectivity measurements show shorter carrier lifetimes in the (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs, attributed to a higher density of antisite defects. It is noteworthy that room temperature Hall measurements imply that the mobility of (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs grown at a low temperature of 250 °C via the MEE mode is superior to that of InGaAs/Be-doped InAlAs MQWs grown in the conventional MBE growth mode, reaching 2230 cm²/V.s. The reason for the higher mobility of (InAs)₄(GaAs)₃/Be-doped InAlAs MQWs is that this short-period superlattice structure can effectively suppress alloy scattering caused by the arbitrary distribution of In and Ga atoms during the growth process of the InGaAs ternary alloy. These results exhibit the promise of the MEE growth approach for growing high-performance MQWs for advanced optoelectronic applications, notably for high-speed optoelectronic devices like THz photoconductive antennas.