Deep eutectic solvents (DESs) composed of choline chloride as hydrogen bond acceptors (HBAs) and six organic acids as hydrogen bond donors (HBDs) were used to extract lignin from bamboo (Phyllostachys edulis (Carrière) J. Houz.). The structures of the DES-extracted lignin samples were analyzed by Fourier-transform infrared spectroscopy (FT-IR), UV–visible spectroscopy (UV–vis), thermogravimetric analysis (TG), and gel permeation chromatography (GPC) to investigate the relationship between the chemical structure of lignin and its antioxidant activity. The results showed that DES treatment removed a large portion of the lignin (73.37–86.38%) from bamboo, and the chemical structure of lignin was changed due to the use of different types of HBDs. The extracted lignin exhibited good UV–vis light shielding properties, thermal stability, and antioxidant activity. Moreover, the total phenolic hydroxyl content of lignins was positively correlated with their antioxidant activity, while the molecular weight of lignins was negatively correlated with their antioxidant activity. Notably, lignin extracted with choline chloride-p-toluenesulfonic acid had the highest phenolic hydroxyl content and lower molecular weight, showing the strongest antioxidant activity (IC50 DPPH = 417.69 μg/mL, IC50 ABTS = 58.62 μg/mL). This study confirms the high thermal stability, excellent antioxidant activity, and UV shielding properties of lignin extracted with choline chloride-organic acid DESs, suggesting its potential application in the fields of antioxidants and material modifiers.

To prepare a low-formaldehyde soy-based adhesive with good water resistance, phenol-formaldehyde modified with glutaraldehyde (PFG) with lower free phenol and free formaldehyde contents was used to cross-link the soy-based adhesive. The results showed that the mechanical properties and water resistance of plywood prepared with soy-based adhesive with PFG was better than that of plywood with the same amount of phenol-formaldehyde (PF). The reaction between phenol and glutaraldehyde was proved by ¹³C-NMR. Under the optimized preparation conditions for plywood, that is to say, press temperature 160 °C, press time 4 min and resin loading 320 g·m⁻², type I plywood could be prepared with 9% PFG as a cross-linker of soy-based adhesive. The Differential Scanning Calorimetry (DSC) result confirmed the cross-linking reaction between soy-based adhesive and PFG or PF. The activation energy of soy-based adhesive with cross-linker PFG was higher than that with PF resin.

To find the effects of cross-linker phenol-formaldehyde (PF) resin on the performance of soy-based adhesives, the reaction between model compounds hydroxymethyl phenol (HPF) and glutamic acid were studied in this paper. HPF prepared in laboratory conditions showed higher content of hydroxymethyl groups than normal PF resin, which was proved by the results of Electrospray Ionization Mass Spectrometry (ESI-MS) and ¹³C Nuclear Magnetic Resonance (¹³C-NMR). The results of ESI-MS, Fourier transform infrared spectroscopy (FT-IR), and ¹³C-NMR based on resultant products obtained from model compounds showed better water resistance of the soy protein-based adhesive modified by PF-based resin, which indicated the reaction between PF resin and soy protein. However, it seemed that the soy-based adhesive cross-linked by HPF with the maximum content of hydroxymethyl groups did not show the best water resistance.

Fully bio-based adhesives are beneficial to reduce the dependence of the wood adhesive industry on synthetic resins based on petrochemical resources and enhance the market competitiveness of adhesives. A fully bio-based wood adhesive composed of tannin and sucrose was developed and successfully used in the preparation of plywood. Effects of the preparation technology on the bonding strength and water resistance of plywood were investigated, and the properties of the adhesive were analyzed by Fourier transform infrared spectroscopy (FT-IR), thermogravimetry (TG) and X-ray diffraction (XRD) in this study. The results showed that: (1) Compared with other biomass adhesives, tannin–sucrose adhesive had the characteristics of high-solid content and low viscosity, which had the potential to prepare particleboard and fiberboard. (2) A proper mass ratio of tannin to sucrose was key to obtaining a tannin–sucrose adhesive with better properties. (3) The optimum preparation process of tannin–sucrose adhesive for plywood was as follows: hot-pressing temperature of 210 °C, hot-pressing time of 1.2 min/mm, m(tannin):m(sucrose) of 60:40 and adhesive loading of 160 g/m². Under these conditions, the water-resistant bonding strength of the plywood was 0.89 MPa, which met the strength requirements of the Type II standard of plywood in GB/T 17657-2013. (4) The hot-pressing temperature played a decisive role in the tannin–sucrose adhesive, and the good performance of the plywood was maintained when the temperature was 210 °C or above. Thus, the prepared tannin–sucrose adhesive had high-bonding strength, good water resistance and thermal stability.

Understanding the interfacial changes of wood during heat treatment can facilitate the improvement of the bonding and coating processes of heat-treated wood. Steam was used as the medium to modify Pinusmassoniana wood through heat treatment at 160, 180, 200, and 220 °C. Changes to the surface characteristics after heat treatment were characterized by Fourier transform-infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscope (SEM) and contact angle measurement. The results showed that: (1) hemicelluloses were the first to experience degradation at 160 °C, and this degradation was the most intense at 200 °C. The cellulose started experiencing obvious degradation at 200 °C, while there was less degradation of lignin at this temperature. (2) Oxygen-containing groups like hydroxyl and carbonyl were gradually reduced as temperature increased with deepened color and passivated surface. (3) Cellulose crystallinity presented a variable trend of increasing–decreasing–increasing. (4) Surface porosity and roughness of Pinus massoniana wood both increased after heat treatment. (5) The Pinus massoniana wood interface turned from hydrophilic to hydrophobic, and 180 °C was a turning point for the wettability of the Pinus massoniana wood interface.