Strain rate and temperature are influential factors that significantly impact the mechanical properties of long glass fiber-reinforced polypropylene composites. This study aims to investigate the tensile properties of these composites, analyzing the effects of temperature, strain rate, and their interplay on variables such as tensile stress, tensile strength, fracture stress, and fracture morphology through a series of comprehensive tensile experiments. The experimental results demonstrate a notable increase in both tensile strength and tensile fracture stress when the temperature is set at 25 °C, accompanied by strain rates of 10⁻⁴, 10⁻³, 10⁻², and 10⁻¹ s⁻¹. Conversely, a significant decrease is observed in the aforementioned properties when the strain rate is fixed at 10⁻⁴, while varying temperatures of −25 °C, 0 °C, 25 °C, 50 °C, and 75 °C are applied. At lower temperatures, cracks manifest on the fracture surface, while matrix softening occurs at higher temperatures. Additionally, in the context of strain rate–temperature coupling, the decreasing trend of both tensile strength and tensile fracture stress decelerates as the temperature ranges from −25 °C to 75 °C at a strain rate of 10⁻¹, compared to 10⁻⁴ s⁻¹. These findings highlight the significant influence of both strain rate and temperature on high fiber content long glass fiber-reinforced polypropylene composites.

Taking austenitic stainless-steel bellows as the research object, a finite element model for the heat treatment of austenitic stainless-steel bellows was constructed based on ABAQUS CAE 2022. The physical properties of the bellows after the heat treatment were analyzed using experimental and simulated curve processing analysis methods. The changes in residual stress and deformation in relation to the bellows under different cooling times were explored, as well as the distribution of residual stress and deformation at a certain cooling time. The results show that as the cooling time of the heat treatment increases, the residual stress of the bellow decreases significantly, the reduction rate accelerates, and the degree of deformation gradually decreases. When the cooling time of the heat treatment is 900 s, the residual stress of the wave peak in the middle position of the bellow is relatively small, and the residual stress value of the wave valley along the axis direction does not change significantly. The deformation degree of the wave peak and valley axis direction is relatively uniform.

Using metal additive manufacturing processes can make up for traditional forging technologies when forming complex-shaped parts. At the same time, metal additive manufacturing has a fast forming speed and excellent manufacturing flexibility, so it is widely used in the aerospace industry and other fields. The fatigue strength of metal additive manufacturing is related to the microstructure of the epitaxially grown columnar grains and crystallographic texture. The crystal plasticity finite element method is widely used in the numerical simulation of the microstructure and macro-mechanical response of materials, which provides a strengthening and toughening treatment and can reveal the inner rules of material deformation. This paper briefly introduces common metal additive manufacturing processes. In terms of additive manufacturing fatigue, crystal plasticity simulations are summarized and discussed with regard to several important influencing factors, such as the microstructure, defects, surface quality, and residual stress.