The paper presents results of investigations on the binderless nanostructured tungsten carbide (WC) cutting tools fabrication and performance. The scientific novelty includes the description of some regularities of the powder consolidation under electric current and the subsequent possibility to utilize them for practical use in the fabrication of cutting tools. The sintering process of WC nanopowder was performed with the electroconsolidation method, which is a modification of spark plasma sintering (SPS). Its advantages include low temperatures and short sintering time which allows retaining nanosize grains of ca. 70 nm, close to the original particle size of the starting powder. In respect to the application of the cutting tools, pure WC nanostructure resulted in a smaller cutting edge radius providing a higher quality of TiC/Fe machined surface. In the range of cutting speeds, v_c = 15–40 m/min the durability of the inserts was 75% of that achieved by cubic boron nitride ones, and more than two times better than that of WC-Co cutting tools. In additional tests of machining 13CrMo4 material at an elevated cutting speed of v_c = 100 m/min, binderless nWC inserts worked almost three times longer than WC-Co composites.

High-frequency electromagnetic fields can have a negative effect on both the human body and electronic devices. The devices and systems utilized in radio communications constitute the most numerous sources of electromagnetic fields. The following research investigates values of the electric component of electromagnetic field intensification determined with the ESM 140 dosimeter during the flights of four aircrafts—Cessna C152, Cessna C172, Aero AT3 R100, and Robinson R44 Raven helicopter—from the airport in Depultycze Krolewskie near Chelm, Poland. The point of reference for the obtained results were the normative limits of the electromagnetic field that can affect a pilot in the course of a flight. The maximum value registered by the dosimeter was E = 3.307 V/m for GSM 1800 frequencies.

Fabrication of alumina–tungsten carbide nanocomposite was investigated. Characteristics of the densification and sintering were analyzed considering both the nano-size particle starting powders and the processing stages. Different heating rates were generated during densification and consolidation with a maximal load was applied only after a temperature of 1000 °C was reached. Due to the varying dominance of different physical processes affecting the grains, appropriate heating rates and pressure at different stages ensured that a structure with submicron grains was obtained. With directly applied alternating current, it was found that the proportion Al₂O₃ (50 wt.%)–WC provided the highest fracture toughness, and a sintering temperature above 1600 °C was found to be disadvantageous. High heating rates and a short sintering time enabled the process to be completed in 12 min, saving energy and time.