Active food packaging is a dynamic area where the scientific community and industry have been trying to find new strategies to produce innovative packaging that is economically viable and compatible with conventional production processes. The materials used to develop active packaging can be organized into scavenging and emitting materials, and based on organic and inorganic materials. However, the incorporation of these materials in polymer-based flexible packaging is not always straightforward. The challenges to be faced are mainly related to active agents’ sensitivity to high temperatures or difficulties in dispersing them in the high viscosity polymer matrix. This review provides an overview of methodologies and processes used in the production of active packaging, particularly for the production of active flexible films at the industrial level. The direct incorporation of active agents in polymer films is presented, focusing on the processing conditions and their effect on the active agent, and final application of the packaging material. Moreover, the incorporation of active agents by coating technologies and supercritical impregnation are presented. Finally, the use of carriers to help the incorporation of active agents and several methodologies is discussed. This review aims to guide academic and industrial researchers in the development of active flexible packaging, namely in the selection of the materials, methodologies, and process conditions.

In this work, alpha-tocopherol (α-TOC) was encapsulated in poly(lactic acid) nanoparticles (PLA NPs) and added to low-density polyethylene (LDPE) films with the aim of producing an active film for food packaging applications. PLA NPs loaded with α-TOC were produced through nanoprecipitation and dried using two methods (freeze-dryer and oven). LDPE-based films with final polymeric matrix concentrations of 10 and 20 g/kg were then produced through blow extrusion. The results showed that LDPE-based films loaded with α-TOC can be produced using blow extrusion, and a good distribution of PLA NPs can be obtained within the LDPE matrix as observed using scanning electron microscopy (SEM). The mechanical properties were affected by the incorporation of α-TOC and PLA NPs loaded with α-TOC, with the observation of a decrease in tensile strength and Young’s Modulus values and an increase in elongation at break. Regarding water vapor permeability, the films showed a reduction in the values with the addition of α-TOC and PLA NPs loaded with α-TOC compared to the LDPE film (control). Films with α-TOC in the free state and loaded in PLA NPs showed antioxidant activity, but their behavior was affected by the encapsulation process.