MXenes are a family of two-dimensional nanomaterials. Titanium carbide MXene (Ti₃C₂T_x-MXene), reported in 2011, is the first inorganic compound reported among the MXene family. In the present work, we report on the study of the composition and various physical properties of Ti₃C₂T_x-MXene nanomaterial, as well as their temperature evolution, to consider MXenes for space applications. X-ray diffraction, thermal analysis and mass spectroscopy measurements confirmed the structure and terminating groups of the MXene surface, revealing a predominant single OH layer character. The temperature dependence of the specific heat shows a Debye-like character in the measured range of 2 K–300 K with a linear part below 10 K, characteristic of conduction electrons of metallic materials. The electron density of states (DOS) calculations for Ti₃C₂OH-MXene reveal a significant DOS value at the Fermi level, with a large slope, confirming its metallic character, which is consistent with the experimental findings. The temperature dependence of electrical resistivity of the MXene samples was tested for a wide temperature range (3 K–350 K) and shows a decrease on lowering temperature with an upturn at low temperatures, where negative magnetoresistance is observed. The magnetoresistance versus field is approximately linear and increases its magnitude with decreasing temperature. The magnetization curves are straight lines with temperature-independent positive slopes, indicating Pauli paramagnetism due to conduction electrons.

Coating of nanoparticles with gallates renders them antioxidant and enhances cellular internalization. In this study, (amino)silica magnetic particles modified with tannic acid (TA) and optionally with chitosan (CS) were developed, and their physicochemical properties and antioxidant activity were evaluated. The results demonstrated that the TA-modified aminosilica-coated particles, as well as the silica-coated particles with a double TA layer, exhibited high antioxidant activity, whereas the silica-coated particles with no or only a single TA layer were well-internalized by LN-229 cells. In addition, a magnet placed under the culture plates greatly increased the cellular uptake of all TA-coated magnetic nanoparticles. The coating thus had a considerable impact on nanoparticle–cell interactions and particle internalization. The TA-coated magnetic nanoparticles have great potential as intracellular carriers with preserved antioxidant activity.

A study of Ti₃Al_1−xSi_xC₂ (x = 0 to x = 1) MAX-phase alloys is reported. The materials were obtained from mixtures of Ti₃AlC₂ and Ti₃SiC₂ powders with hot pressing sintering technique. They were characterised with X-ray diffraction, heat capacity, electrical resistivity, and magnetoresistance measurements. The results show a good quality crystal structure and metallic properties with high residual resistivity. The resistivity weakly varies with Si doping and shows a small, positive magnetoresistance effect. The magnetoresistance exhibits a quadratic dependence on the magnetic field, which indicates a dominant contribution from open electronic orbits. The Debye temperatures and Sommerfeld coefficient values derived from specific heat data show slight variations with Si content, with decreasing tendency for the former and an increase for the latter. Experimental results were supported by band structure calculations whose results are consistent with the experiment concerning specific heat, resistivity, and magnetoresistance measurements. In particular, they reveal that of the s-electrons at the Fermi level, those of Al and Si have prevailing density of states and, thus predominantly contribute to the metallic conductivity. This also shows that the high residual resistivity of the materials studied is an intrinsic effect, not due to defects of the crystal structure.