In recent years, asphalt pavement has been subjected to varied environmental conditions during its service life, conditions that predispose it to deformation and cracking. To enhance the performance of asphalt pavement, rock asphalt has been selected as a modifier due to its good compatibility with virgin asphalt binder and its ability to improve the fatigue cracking resistance of asphalt mixtures. Although scholars have conducted some studies on rock asphalt mixtures, research on the fatigue and self-healing performance of these mixtures under conditions such as ultraviolet (UV) aging and freeze–thaw remains limited. This paper presents findings from a study that employs a combined fatigue-healing test to assess the impact of such complex environmental factors on the fatigue and self-healing properties of fine aggregate matrix (FAM) mixtures containing three types of rock asphalts, i.e., Buton, Qingchuan (QC), and Uintaite Modifier (UM). The analysis of fatigue-healing test results, grounded in viscoelastic continuum damage (VECD) theory, indicates that rock asphalt can extend the fatigue life of FAM mixtures, albeit with a concomitant decrease in their self-healing capabilities. The study further reveals that UV aging, freeze–thaw, and UV aging–freeze–thaw conditions all led to a diminution in the fatigue and self-healing properties of FAM mixtures. However, FAM mixtures containing rock asphalt demonstrated greater resilience against these reductions. Atomic force microscope (AFM) results indicate that UV aging reduced the number of bee-structures and enlarged their area, whereas the incorporation of rock asphalt enhanced the uniformity of these structures’ distribution, thereby improving the fatigue cracking resistance of FAM mixtures. Fourier transform infrared spectroscopy (FTIR) analysis reveals that while UV aging increased the carbonyl and sulfoxide indices within the asphalt binder, rock asphalt is effective in mitigating this effect to a certain degree, thereby enhancing the aging resistance of FAM mixtures.

As a green and low-carbon road material, warm-mix rubber asphalt (WMRA) has received extensive attention from scholars for its road performance. In the in-depth study of its properties, the fatigue characteristics of WMRA are particularly critical. However, in current studies on asphalt fatigue performance, its self-healing ability is often underestimated or neglected. Furthermore, the simplified viscoelastic continuum damage theory (S-VECD), with its accuracy, speed, and convenience, provides a powerful tool for analyzing asphalt fatigue performance. Therefore, to analyze the fatigue and self-healing performances of WMRA in practical applications, four sample materials were selected in this study: virgin asphalt mastic (VAM), rubber asphalt mastic (RAM), Sasobit rubber asphalt mastic (SRAM), and Evotherm rubber asphalt mastic (ERAM). Subsequently, the samples were subjected to a comprehensive experimental design with frequency sweep tests, linear amplitude sweep tests, and multiple intermittent loading time sweep tests under different aging conditions. The fatigue and self-healing performances of different aging degrees and different types of WMRA were evaluated based on the S-VECD theory. The results show that aging reduces the fatigue and self-healing performances of asphalt mastic to a certain extent, and at a 7% strain, the fatigue life of SRAM after long-term aging is only 30.7% of the life of the unaged sample. The greater the aging degree, the more pronounced the effect. Under different aging levels, the warm-mix agent can significantly improve the fatigue and self-healing performances of rubber asphalt mastic. After undergoing ten fatigue intermittent loading tests, the recovery rate of the complex shear modulus for the long-term aged VAM was 0.65, which is lower than that of SRAM under the same conditions, and the warm mix can further extend the fatigue life of rubber asphalt by improving the self-healing properties of the asphalt. The role of Sasobit in enhancing the fatigue and self-healing performances of rubber asphalt mastic is more significant. This study can provide a theoretical basis for the promotion and application of WMRA pavements and contribute to the sustainable development of road construction.

Moisture accelerates the degradation of asphalt properties, significantly impacting the service life of roads. Therefore, this study uses simplified viscoelastic continuous damage theory and employs frequency scanning, linear amplitude scanning, and fatigue–healing–fatigue tests with a dynamic shear rheometer. The objective is to investigate the effects of aging time, moisture conditions, and aging temperature on the fatigue and self-healing performance of SBS (Styrene–Butadiene–Styrene block copolymer)-modified asphalt, nano-SiO₂-modified asphalt, and nano-SiO₂/SBS composite modified asphalt in a moisture-rich environment. The results indicate that nano-SiO₂ powder enhances the low-temperature performance of modified asphalt, whereas the SBS modifier reduces temperature sensitivity and increases the recovery percentage after deformation. Compared to SBS-modified asphalt, the deformation resistance of nano-SiO₂/SBS composite modified asphalt has increased by about 30%, while nano-SiO₂-modified asphalt shows relatively poor deformation resistance. The fatigue performance of SBS-modified asphalt deteriorates under moisture, whereas the addition of nano-SiO₂ powder improves its fatigue life. Nano-SiO₂/SBS composite modified asphalt exhibits strong self-healing capabilities. Although self-healing can enhance the fatigue life of modified asphalt, moisture inhibits this improvement after self-healing.