The microstructure, phase composition, and mechanical properties during heat treatment and rolling of the novel Al-5.0Cu-3.2Er-0.9Mn-0.3Zr alloy were evaluated. A new quaternary (Al,Cu,Mn,Er) phase with possible composition Al₂₅Cu₄Mn₂Er was found in the as-cast alloy. Al₂₀Cu₂Mn₃ and Al₃(Zr,Er) phases were nucleated during homogenization, and θ″(Al₂Cu) precipitates were nucleated during aging. The metastable disc shaped θ″(Al₂Cu) precipitates with a thickness of 5 nm and diameter of 100–200 nm were nucleated mostly on the Al₃(Zr,Er) phase precipitates with a diameter of 35 nm. The hardness Vickers (HV) peak was found after the annealing of a rolled alloy at 150 °C due to strengthening by θ″(A₂Cu) precipitates, which have a larger effect in materials hardness than do the softening processes. The novel Al-Cu-Er-Mn-Zr alloy has a yield strength (YS) of 320–332 MPa, an ultimate tensile strength (UTS) of 360–370 MPa, and an El. of 3.2–4.0% in the annealed alloy after rolling condition.

The mechanical properties and microstructure of as-cast and homogenized AA7075 were investigated. This alloy was modified by adding transition elements 0.3%Sc + 0.5%Zr, 1%Ti + 0.2%B, and 1%Fe + 1%Ni for use in additive manufacturing applications. After adding Ti + B and Sc + Zr, the structure became uniform and finer with the formation of the Al₃(Sc, Zr) and TiB₂ phases. Coarse structures were obtained with the formation of an extremely unfavorable morphology, close to a needle-like structure when Fe + Ni was added. The mechanical properties of the modified alloys were increased compared to those of the standard alloy, where the best ultimate tensile strength (UTS) and yield strength (YS) were obtained in the AA7075-TiB alloy compared to the standard alloy in as-cast and homogenized conditions, and the highest hardness value was provided by Fe + Ni additives. The effect of the laser melting process on the microstructure and mechanical properties was investigated. Single laser melts were performed on these alloys using 330 V and a scanning speed of 8 mm/s. During the laser melting, the liquation of the alloying elements occurred due to non-equilibrium solidification. A change in the microstructures was observed within the melt zone and heat-affected zone (HAZ). The hardness of the laser-melted zone (LMZ) after adding the modification elements was increased in comparison with that of the standard alloy. Corrosion testing was performed using a solution of 100 mL distilled water, 3.1 g NaCl, and 1 mL HCl over 5, 10, and 30 min and 1 and 2 h. The corrosion resistance of the alloy modified with FeNi was low because of the non-uniform elemental distribution along the LMZ, but in the case of modification with ScZr and TiB, the corrosion resistance was better compared to that of the standard alloy.

The effect of zirconium on the microstructure, phase composition, and mechanical properties of AlCuYb and AlCuGd alloys was studied. The microstructure of the as-cast alloys did not consist of new intermetallic phases of zirconium with other elements, so the zirconium was fully dissolved in the aluminum matrix. The AlCuYbZr/AlCuGdZr alloys demonstrated higher hardness values compared to the AlCuYb/AlCuGd alloys due to the precipitation of the Al₃(Zr,Yb) and Al₃(Zr,Gd) phases, which were formed during the homogenization treatment. The AlCuYbZr alloy had a 10–20 MPa higher yield and tensile strength than the AlCuGdZr alloy at the same annealing temperature and time. The AlCuYbZr alloy exhibited good mechanical tensile properties at an annealing temperature of 100 °C for 1 h, with a yield strength of 276 MPa, ultimate tensile strength of 312 MPa, and elongation of 3.1%, while the as-rolled AlCuGdZr alloy had similar mechanical tensile properties, with a yield strength of 279 MPa, ultimate tensile strength of 307 MPa, and elongation of 4.8%. At an annealing temperature of 300 °C for 10 min, The AlCuYbZr and AlCuGdZr alloys showed a good ductility of 10.5% and 8%, respectively, with 207 MPa yield strength for both alloys. AlCuYbZr and AlCuGdZr alloys are a prospective base composition for developing novel high technology heat resistant aluminum alloys.