The microstructure, phase composition, and mechanical properties during heat treatment and rolling of the novel Al-5.0Cu-3.2Er-0.9Mn-0.3Zr alloy were evaluated. A new quaternary (Al,Cu,Mn,Er) phase with possible composition Al₂₅Cu₄Mn₂Er was found in the as-cast alloy. Al₂₀Cu₂Mn₃ and Al₃(Zr,Er) phases were nucleated during homogenization, and θ″(Al₂Cu) precipitates were nucleated during aging. The metastable disc shaped θ″(Al₂Cu) precipitates with a thickness of 5 nm and diameter of 100–200 nm were nucleated mostly on the Al₃(Zr,Er) phase precipitates with a diameter of 35 nm. The hardness Vickers (HV) peak was found after the annealing of a rolled alloy at 150 °C due to strengthening by θ″(A₂Cu) precipitates, which have a larger effect in materials hardness than do the softening processes. The novel Al-Cu-Er-Mn-Zr alloy has a yield strength (YS) of 320–332 MPa, an ultimate tensile strength (UTS) of 360–370 MPa, and an El. of 3.2–4.0% in the annealed alloy after rolling condition.

The current study observed a grain structure evolution in the central part and periphery of the sample of an Al–Mg–Mn-based alloy during isothermal multidirectional forging (IMF) at 350 °C with a cumulative strain of 2.1–6.3 and a strain per pass of 0.7. A bimodal grain size distribution with areas of fine and coarse grains was observed after IMF and subsequent annealing. The grain structure, mechanical properties, and superplastic behavior of the samples subjected to IMF with a cumulative strain of 6.3 and the samples exposed to IMF with subsequent cold rolling were compared to the samples exposed to a simple thermo-mechanical treatment. The micro-shear bands were formed inside original grains after the first three passes. The fraction of recrystallized grains increased and the mean size decreased with an increasing cumulative strain from 2.1 to 6.3. Significant improvements of mechanical properties and superplasticity were observed due to the formation of a homogenous fine grain structure 4.8 µm in size after treatment including IMF and subsequent cold rolling.