Water-lubricated material is the fundamental ingredient of a water-lubricated bearing (WLB), of which the friction and wear properties directly affect the working performance and service life of a WLB. We designed a micron-scale stripe texture and fabricated a negative microtexture mold by femtosecond laser etching. The microtextures were fabricated onto the surface of Thordon and polyurethane water-lubricated materials by a precision thermoforming machine. Tribological tests showed that the microstripe texture on water-lubricated materials had lower friction and wear properties than that on pristine surface materials. The results demonstrated that the presence of the microstripe texture effectively improved the friction and anti-wear properties of the water-lubricated materials. This study provides a new idea for the design and preparation of water-lubricated materials with good water-lubricating and anti-wear properties.

The mechanism of the combined process of ion beam sputtering (IBS) and HF acid etching on the chemical structure defects of fused silica and its laser damage resistance performance were investigated in this paper. During the removal process of surface material, the sputtering effect causes lattice atoms to flee their native space locations, and a large amount of unsaturated chemical structures are produced on the silica surface, which improves the chemical activity of Si and O atoms, accelerates the chemical reaction process between surface atoms and water molecules, increases the content of hydroxyl groups (OH-) in the shallow layer, and enhances the photothermal weak absorption intensity. However, the increase in hydroxyl content weakens the binding strength of silicon–oxygen bonds, destroys the spatial network structure of silica bulk, and reduces its mechanical strength, resulting in a decrease in its laser damage resistance performance. The paper reveals for the first time the mechanism by which IBS changes the structure characteristics of silica material, accelerates the surface hydroxylation process, and thereby reduces the laser damage resistance performance. This work provides technical guidance for effectively suppressing chemical structure defects on silica surfaces and improving the laser damage resistance performance of optical components under high-flux laser irradiation.

Oil spill cleanup in water remains a critical challenge due to the harmful secondary pollution from conventional methods such as burning or chemical degradation. Herein, we present a facile method to fabricate a superhydrophobic and superoleophilic polyurethane (PU) foil for efficient and environmentally friendly oil/water separation. More specifically, micropillar arrays were embedded onto the foil surface through a nanoimprinting process. Microporous structures were generated at the foil cross-section by a supercritical carbon dioxide (CO₂) saturation method. The dimensions of pillar and pore structures were optimized with the aim of boosting selective wetting (i.e., water repellency and oil attraction) properties. As a result, the developed PU foil shows an oil absorption efficiency nearly 4 times higher than a pristine reference. Moreover, the structured PU foil stably retains the absorbed oil for over a week, demonstrating an absorption capacity of nearly 400%, which is also much superior than the unstructured sample. Our concept of combining both topographical micropillars and cross-sectional micropores onto PU foil provides a novel approach for achieving efficient and environmental friendly oil/water separation.

In this paper, the mechanism of combined process of ion beam sputtering (IBS) and HF acid etching on the chemical structure defects of fused silica and its laser damage resistance perfor-mance were investigated. During the removal process of surface material, the sputtering effect causes lattice atoms to detach from their original positions, forming a large number of unsaturated structures on silica surface, which improves the chemical activity of Si and O atoms, accelerates the chemical reaction process between surface atoms and water molecules, increases the content of hydroxyl (OH-) groups in the shallow layer, and enhances the photothermal weak absorption intensity. However, the presence of OH- groups reduces the bonding strength of Si-O, destroys the spatial network structure of silica bulk, and reduces the mechanical strength of silica surface, resulting in a decrease in its laser damage resistance performance. The paper reveals for the first time the mechanism of IBS to change the structure characteristics of silica material, accelerate the surface hydroxylation process, and thereby reduces the laser damage resistance performance. This work provides technical guidance for effectively suppressing chemical structure defects on silica surface and improving laser damage resistance performance of optical components under high-flux laser irradiation.