In recent years, high-entropy alloys have attracted increasing scientific interest. Due to their promising combination of properties, such as high hardness and high temperature stability, they are attractive for use as tool coatings for machining applications, to give but one example. Previous studies often focused on layer deposition using magnetron sputtering. Comparatively little research has been carried out to date on coating deposition using direct current cathodic vacuum arc deposition (CAE), with higher achievable rates and almost completely ionized plasmas. The aim of this work is to investigate (HfNbTaTiZr)N-coatings produced by CAE. The nitrogen content was varied and the effects on the coating properties were investigated. Changing the N₂/(N₂ + Ar) ratio between 0.1 and 1.0 and varying the working pressure in the chamber from 2 Pa to 5 Pa resulted in variations of the nitrogen content of the coatings, ranging from 30 at% to 50 at%. Although different microstructures of the coatings were obtained, there was only a minor influence on the hardness and Young’s modulus.

The very high cycle properties of Inconel 718 in two different heat treatment conditions were investigated at a test temperature of 500 °C. One condition was optimized for fatigue strength and displayed a finer-grained microstructure, while the second batch had a more coarse-grained microstructure. For the high-temperature ultrasonic fatigue testing, a new test concept was developed. The method is based on the principle of a hot-air furnace and thus differs from the conventionally used induction heaters. The concept could be successfully evaluated in the course of the investigations. The materials’ microstructure was analyzed before and after fatigue testing by means of metallographic and electron backscatter diffraction (EBSD)analysis. The results show a significant influence of the heat treatment on the fatigue strength caused by the specific microstructure. Further, a difference in crack propagation behavior due to microstructural influences and non-metallic precipitations was observed.